Titanium-Group Nano-Whiskers and Method of Production
Disclosed herein are structures comprising a titanium, zirconium, or hafnium powder particle with titanium carbide, zirconium carbide, or hafnium carbide (respectively) nano-whiskers disposed adjacent and anchored to the powder particle. Also disclosed are methods for fabrication of such structures, involving heating the powder particles and exposing the particles to an organic gas.
1 . A method of forming titanium group nano-whiskers comprising:
disposing titanium-group powder particles in a furnace chamber;
establishing a controlled environment for the titanium-group powder particles;
heating the titanium-group powder particles in the controlled environment to a temperature that is in a temperature range from approximately 600° C. to approximately 650° C., establishing heated titanium-group powder particles; and
exposing the heated titanium-group powder particles to an organic gas for a duration of time that is in a time range from about one hour to about twenty-four hours, wherein the titanium group nano-whiskers are formed adjacent and anchored to the titanium-group powder particles.
2 . The method of claim 1 wherein the step of establishing a controlled environment consists of establishing a protective reducing environment.
3 . The method of claim 1 wherein the step of establishing a controlled environment consists of establishing an inert environment.
4 . The method of claim 1 wherein the step of establishing a controlled environment consists of establishing an oxidizing environment.
5 . The method of claim 1 wherein the titanium-group powder particles comprise titanium and the titanium group nano-whiskers comprise titanium carbide.
6 . The method of claim 1 wherein the titanium-group powder particles comprise zirconium and the titanium group nano-whiskers comprise zirconium carbide.
7 . The method of claim 1 wherein the titanium-group powder particles comprise hafnium and the titanium group nano-whiskers comprise hafnium carbide.
8 . The method of claim 1 wherein exposing the heated titanium-group powder particles to the organic gas comprises flowing the organic gas around the titanium-group powder particles.
9 . A titanium-group structure comprising:
a titanium-group powder particle having a maximum dimension that is in a first range from about one micron to about 500 microns; and
a plurality of titanium group nano-whiskers disposed adjacent and anchored to the titanium-group powder particle, the titanium group nano-whiskers having a tapered structure with a maximum diameter that is in a second range from about one nanometer to about one hundred nanometers and having a length that is at least about one hundred nanometers.
10 . The titanium-group structure of claim 9 wherein the titanium-group powder particle comprises titanium and the titanium group nano-whiskers comprise titanium carbide.
11 . The titanium-group structure of claim 9 wherein the titanium-group powder particle comprises zirconium and the titanium group nano-whiskers comprise zirconium carbide.
12 . The titanium-group structure of claim 9 wherein the titanium-group powder particle comprises hafnium and the titanium group nano-whiskers comprise hafnium carbide.