Biodegradable composite wire for medical devices
View Patent ↗A bimetal composite wire including, in cross-section, an outer shell or tube formed of a first biodegradable material and an inner core formed of a second biodegradable material. When formed into a stent, for example, the first and second biodegradable materials may be different, and may have differing biodegradation rates. In a first embodiment, the first biodegradable material of the shell may degrade relatively slowly for retention of the mechanical integrity of a stent during vessel remodeling, and the second biodegradable material of the core may degrade relatively quickly. In a second embodiment, the first biodegradable material of the shell may degrade relatively quickly, leaving a thinner structure of a second biodegradable material of the core that may degrade relatively slowly. The biodegradation rates may be inherently controlled, such as by selection of materials, and also may be mechanically controlled, such as by material thicknesses and the geometric configuration of the shell, core, or overall device. In any embodiment, the metallic scaffold may also be coated with a drug-eluting, biodegradable polymer, to further inhibit neointimal proliferation and/or restenosis.
1. A bimetal composite wire, comprising:
a drawn outer shell formed of a first biodegradable metallic material, said shell defining an inner shell diameter and an outer shell diameter; and
a drawn inner core formed of a second biodegradable metallic material, said inner core defining an outer core diameter,
said first and second biodegradable metallic materials being different from one another whereby said first and second biodegradable metallic materials have differing biodegradation rates, and
said inner shell diameter of said outer shell substantially equal to said outer core diameter such that, when viewed in section, said inner core completely fills said outer shell, said outer shell formed as a uniform and continuous jacket such that said wire may be coiled, braided, or stranded.
2. The bimetal composite wire of claim 1 , wherein said first biodegradable material is selected from the group consisting of pure metallic iron (Fe) and an iron-based alloy (Fe alloy), and said second biodegradable material is selected from the group consisting of pure magnesium (Mg) and a magnesium-based alloy (Mg alloy).
3. The bimetal composite wire of claim 1 , wherein said first biodegradable material is selected from the group consisting of pure magnesium (Mg) and a magnesium-based alloy (Mg alloy), and said second biodegradable material is selected from the group consisting of pure metallic iron (Fe) and an iron-based alloy (Fe alloy).
4. The bimetal composite wire of claim 1 , having a ratio of yield strength to elastic modulus of at least 0.5%.
5. The bimetal composite wire of claim 1 , having a fatigue strength of 10 7 cycles at an alternating strain level of 0.2.
6. The bimetal composite wire of claim 1 , having a ductility characterized by the ability to form the wire over a mandrel diameter equal to or less than 20 times the outside diameter of the bimetal composite wire.
7. The bimetal composite wire of claim 1 , having:
a ratio of yield strength to elastic modulus of at least 0.5%;
a fatigue strength of 10 7 cycles at an alternating strain level of 0.2; and
a ductility characterized by the ability to form the wire over a mandrel diameter equal to or less than 20 times the outside diameter of the bimetal composite wire.
8. A stent made of the bimetal composite wire of claim 1 .
9. A bimetal composite wire, comprising:
a drawn outer shell comprising a first biodegradable metallic material, said outer shell making up a percentage of a total cross-sectional area within an outer shell diameter defined by said outer shell; and
a drawn inner core comprising a second biodegradable metallic material, said inner core making up the balance of the total cross-sectional area,
said first and second biodegradable metallic materials being different from one another whereby said first and second biodegradable metallic materials have differing biodegradation rates.
10. The bimetal composite wire of claim 9 , wherein:
said outer shell defines an inner shell diameter, and
said inner core defines an outer core diameter,
said inner shell diameter of said outer shell substantially equal to said outer core diameter such that, when viewed in section, said inner core completely fills said outer shell.
11. The bimetal composite wire of claim 9 , wherein said inner core comprises a solid metallic wire core and said outer shell comprises a tube.
12. The bimetal composite wire of claim 9 , wherein said first biodegradable material is selected from the group consisting of pure metallic iron (Fe) and an iron-based alloy (Fe alloy), and said second biodegradable material is selected from the group consisting of pure magnesium (Mg) and a magnesium-based alloy (Mg alloy).
13. The bimetal composite wire of claim 9 , wherein said first biodegradable material is selected from the group consisting of pure magnesium (Mg) and a magnesium-based alloy (Mg alloy), and said second biodegradable material is selected from the group consisting of pure metallic iron (Fe) and an iron-based alloy (Fe alloy).
14. The bimetal composite wire of claim 9 , wherein said outer shell diameter is between 20 μm and 250 μm.
15. A bimetal composite wire, comprising:
a drawn outer shell formed of a first biodegradable metallic material, said outer shell comprising a tube defining an inner shell diameter and an outer shell diameter and making up a percentage of a total cross-sectional area of said wire; and
a drawn inner core formed of a second biodegradable metallic material, said inner core comprising a solid metallic wire defining a core diameter and making up the balance of the cross-sectional area of said wire,
said first and second biodegradable metallic materials being different from one another whereby said first and second biodegradable metallic materials have differing biodegradation rates,
said inner shell diameter of said outer shell substantially equal to said outer core diameter of said inner core such that, when viewed in section, said inner core completely fills said outer shell, and
said bimetal wire comprising a continuous wire structure capable of being spooled.
16. The bimetal composite wire of claim 15 , wherein said first biodegradable material is selected from the group consisting of pure metallic iron (Fe) and an iron-based alloy (Fe alloy), and said second biodegradable material is selected from the group consisting of pure magnesium (Mg) and a magnesium-based alloy (Mg alloy).
17. The bimetal composite wire of claim 15 , wherein said first biodegradable material is selected from the group consisting of pure magnesium (Mg) and a magnesium-based alloy (Mg alloy), and said second biodegradable material is selected from the group consisting of pure metallic iron (Fe) and an iron-based alloy (Fe alloy).
18. The bimetal composite wire of claim 1 , wherein said outer shell makes up a percentage of a total cross-sectional area of said wire, and said inner core makes up the balance of the cross-sectional area of said wire.
19. The bimetal composite wire of claim 1 , wherein said outer shell comprises a tube and said inner core comprises a solid metallic wire core.
20. The bimetal composite wire of claim 1 , wherein said outer shell diameter is between 20 μm and 250 μm.