Method of making implantable medical devices having controlled surface properties
View Patent ↗An implantable medical device that is fabricated from materials that present a blood or body fluid or tissue contact surface that has controlled heterogeneities in material constitution. An endoluminal stent-graft and web-stent that is made of a monolithic material formed into differentiated regions defining structural members and web regions extending across interstitial spaces between the structural members. The endoluminal stent-graft is characterized by having controlled heterogeneities at the blood flow surface of the stent.
1. A method for controlling surface properties of an implantable medical device, comprising:
vacuum depositing a device forming biomaterial selected from one of elemental nickel and elemental titanium or nickel-titanium alloy onto a cylindrical substrate maintained at a temperature range between about 300 to 1100 degrees Centigrade, the substrate having a pre-determined pattern of recesses in an outer surface thereof to form a tubular device forming biomaterial on the cylindrical substrate;
controlling the formation of heterogeneities at a blood or tissue contacting surface of the tubular device forming biomaterial during the vacuum depositing step, such that controlled heterogeneities are formed at the blood or tissue contacting surface; and
removing the medical device from the substrate.
2. The method according to claim 1 , further comprising forming cell-adhesion domains having inter-domain boundaries less than the surface area of a human endothelial cell and wherein the substrate has a coefficient of thermal expansion different than that of the resultant implantable medical device.
3. The method according to claim 1 , wherein the controlled heterogeneities are selected from the group consisting of grain size, grain phase and grain composition and luminal surface topography.
4. The method according to claim 1 , wherein the controlled heterogeneities have a blood contact surface of diameter less than or equal to about 10 μm and an inter-heterogeneity boundary between about 0 and 2 μm.
5. A method for controlling surface properties of an implantable medical device, comprising:
forming a tubular nickel-titanium alloy biomaterial onto a substrate maintained at a temperature range between about 300 to 1100 degrees Centigrade and non-zero bias voltage present between about −1000 and +1000 volts applied to the generally cylindrical substrate sufficient to impart a hyperthermal energy of energetic species arriving at the surface of the substrate to between about 0.1 eV and about 700 eV, the substrate having a pre-determined pattern of topographical features on an exterior surface thereof, wherein the pattern of topographical features comprises a positive or negative pattern that is imparted to the device forming biomaterial;
controlling the formation of heterogeneities at a blood or tissue contacting surface of the biomaterial by fabricating the bulk material of the medical device to have a defined grain sizes that yield sites along the surface of the medical device having protein binding capability, wherein the controlled heterogeneities have a blood contact surface of diameter less than or equal to about 10 μm and an inter-heterogeneity boundary between about 0 and 2 μm; and
removing the medical device from the substrate.
6. The method according to claim 5 , wherein the step of controlling the formation of heterogeneities further comprises etching.
7. The method according to claim 5 , further comprising forming cell-adhesion domains having inter-domain boundaries less than the surface area of a human endothelial cell and wherein the substrate has a coefficient of thermal expansion different than that of the resultant medical device.
8. The method according to claim 5 , wherein the controlled heterogeneities are dimensioned to have a blood contact surface area of about less than 6 μm2.
9. The method according to claim 5 , wherein the controlled heterogeneities further include a grain phase and a grain composition.
10. The method according to claim 5 , wherein the controlled heterogeneities are material compositions.
11. The method according to claim 5 , wherein the implantable medical device is a tubular device and the controlled heterogeneities are on the luminal surface topography.
12. A method for controlling surface properties of an implantable medical device, comprising:
vacuum depositing a generally tubular nickel-titanium alloy device onto a substrate, the substrate having a pre-determined pattern of recesses and the substrate is maintained at a non-zero bias voltage present between about −1000 and +1000 volts applied to the generally cylindrical substrate sufficient to impart a hyperthermal energy of energetic species arriving at the surface of the substrate to between about 0.1 eV and about 700 eV;
controlling the formation of heterogeneities at a blood or tissue contacting surface of the biomaterial during fabrication of the medical device, such that controlled heterogeneities are formed and have a substantially homogeneous surface energy and electrostatic charge across a blood contact surface of the metal film, wherein the controlled heterogeneities have a blood contact surface of diameter less than or equal to about 10 μm and an inter-heterogeneity boundary between about 0 and 2 μm; and
removing the medical device from the substrate.
13. The method according to claim 12 , wherein the controlled heterogeneities are selected from the group consisting of grain size, grain phase and grain composition and luminal surface topography.
14. The method according to claim 12 , wherein the step of controlling the formation of heterogeneities further comprises etching.
15. The method according to claim 12 , wherein the controlled heterogeneities are material compositions.
16. The method according to claim 12 , wherein the substrate has a coefficient of thermal expansion different than that of the resultant medical device.
17. The method according to claim 12 , wherein the substrate is maintained at a temperature range between about 300 to 1100 degrees Centigrade.
18. The method according to claim 5 , wherein the controlled heterogeneities are on the luminal surface.
19. The method according to claim 1 , wherein the controlled heterogeneities are dimensioned to have a blood contact surface area of about less than 6 μm 2 .
20. The method according to claim 1 , wherein the substrate is maintained at a non-zero bias voltage present between about −1000 and +1000 volts applied to the generally cylindrical substrate sufficient to impart a hyperthermal energy of energetic species arriving at the surface of the substrate to between about 0.1 eV and about 700 eV.