Extrusion of glassy aluminum-based alloys
View Patent ↗A method of extruding a glassy aluminum-based alloy billet, by soaking the billet for sufficient time to heat the billet to an extrusion starting temperature of from about 300° F. to about 600° F. and extruding the billet in a streamline die having an extrusion ratio to keep the adiabatic temperature below the starting temperature while maintaining the streamline die at a temperature of about 400° F. to about 600° F. at a ram speed less than that which would raise the streamline die temperature within this range.
1. A method of extruding an aluminum-based alloy, comprising the steps of:
selecting an aluminum-based alloy billet, wherein the aluminum based alloy is selected from the group consisting of a devitrified alloy having a nanocrystalline microstructure and a glassy aluminum alloy having substantially no devitrification;
soaking the billet for sufficient time to heat the billet to an extrusion starting temperature of from about 450° F. to about 550° F. (232.2° C. to 287.9° C.), wherein a time for the soaking is from about 10 minutes to about 72 hours;
extruding the billet in a streamline die having an extrusion ratio sufficient to keep the adiabatic temperature below the starting temperature while maintaining the streamline die at a temperature of about 400° F. to about 600° F. (204.4° C. to 315.6° C.) at a ram speed less than that which would raise the streamline die temperature within this range; and
removing the extruded billet from the die.
2. The method of claim 1 , wherein the aluminum based alloy is an aluminum based alloy containing from 3 to 18.5 atomic percent nickel and 3 to 14.0 atomic percent yttrium.
3. The method of claim 1 , wherein the streamline die is maintained at a temperature ranging from about 400° F. to about 575° F. (204.4° C. to 301.7° C.) at a ram speed of from about 0.1 to 100 inches per minute.
4. The method of claim 1 , wherein the streamline die is maintained at a temperature ranging from about 475° F. to about 525° F. (246.1° C. to 273.9° C.) at a ram speed of from about 0.1 to 5 inches per minute.
5. The method of claim 1 , wherein the streamline die has an extrusion ratio of from about 1 to about 10, and has a length ranging from about 4 inches to 6 inches (10.16 cm. to 15.24 cm.).
6. A method of extruding a devitrified aluminum-based alloy, comprising the steps of:
selecting a devitrified aluminum-based alloy billet having a nanocrystalline microstructure;
soaking the billet having a nanocrystalline microstructure for sufficient time to heat the billet to an extrusion starting temperature of from about 450° F. to about 550° F. (232.2° C. to 287.9° C.), wherein a time for the soaking is from about 10 minutes to about 72 hours;
extruding the billet in a streamline die having an extrusion ratio sufficient to keep the adiabatic temperature below the starting temperature while maintaining the streamline die at a temperature of about 400° F. to about 600° F. (204.4° C. to 315.6° C.) at a ram speed less than that which would raise the streamline die temperature within this range; and
removing the extruded billet from the die.
7. The method of claim 6 , wherein the devitrified aluminum based alloy is an aluminum based alloy containing from 3 to 18.5 atomic percent nickel and 3 to 14.0 atomic percent yttrium.
8. The method of claim 7 , wherein the streamline die is maintained at a temperature ranging from about 400° F. to about 575° F. (204.4° C. to 301.7° C.) at a ram speed of from about 0.1 to 100 inches per minute.
9. The method of claim 6 , wherein the streamline die has an extrusion ratio of from about 1 to about 10, and has a length ranging from about 4 inches to 6 inches (10.16 cm. to 15.24 cm.).