Weathering-stabilized acrylonitrile copolymer molding compositions
The present invention relates to a thermoplastic molding composition comprising a) 77.7% to 99.7% by weight of one or more styrene copolymers, as component A b) 0.1% to 5% by weight of the compounds of the formulae I, II, III, IV, and V, or isomers thereof, as component B: c) 0.2% to 0.7% by weight of a compound of the formula (VI), as component C: d) 0.2% to 0.7% by weight of a mixture of the formula (VII), as component D: e) 0% to 0.5% by weight of a compound of the formula (VIII) as component E: or 0% to 0.5% by weight of a compound of the formula (X): or 0% to 0.5% by weight of a compound of the formula (XI): f) 0% to 10% by weight of one or more additives which are different from components B, C, D, and E, as component F, and the percentage by weight being based in each case on the total weight of components A to F and together making up 100% by weight.
1. A thermoplastic molding composition consisting of
a) 77.7% to 99.7% by weight of one or more styrene copolymers, as component A, wherein component A is a copolymer of acrylonitrile with styrene and/or α-methylstyrene wherein the weight fraction of acrylonitrile, based on component A, is at least 15% and not more than 40%,
b) 0.1% to 5% by weight of at least one compound selected from the group consisting of the formulae I, II, III, IV, V, and isomers thereof, as component B:
c) 0.2% to 0.7% by weight of a compound of the formula (VI), as component C:
d) 0.2% to 0.7% by weight of a mixture of the formula (VII), as component D:
e) 0% to 0.5% by weight of a compound of the formula (VIII) as component E:
f) 0% to 10% by weight of one or more additives which are different from components C, D, and E, as component F, selected from the group consisting of dyes, pigments, colorants, antistats, antioxidants, stabilizers for improving heat stability, stabilizers for enhancing light stability, stabilizers for raising hydrolysis resistance and chemical resistance, agents which act against thermal decomposition, lubricants, and combinations thereof, and
the percentage by weight being based in each case on the total weight of components A to F and together not exceeding 100% by weight, wherein the gloss of the composition, determined in accordance with DIN 67530 from a 60° viewing angle, after 1500 h weathering time is from 62 to 101, and wherein the weight ratio of component C to component D is in the range from 3:1 to 1:1.
2. The thermoplastic molding composition according to claim 1 , wherein the weight fraction of component B is 0.2% to 2% by weight.
3. The thermoplastic molding composition according to claim 1 , wherein the thermoplastic molding composition is used in the exterior area of motor vehicles.
4. The thermoplastic molding composition according to claim 3 , wherein the thermoplastic molding composition is used in motor vehicles in column covers, spoilers, window surrounds, trim strips, cover hood, cover plates, as part of a radiator grill, aerial cover, side mirror or front and tail lights.
5. The thermoplastic molding composition according to claim 1 , wherein components D and E are used in a weight ratio of 2:1 to 0.5:1.
6. The thermoplastic molding composition according to claim 1 , wherein the weight ratio of component C to component D is in the range from 2:1 to 1:1.
7. The thermoplastic molding composition according to claim 6 , wherein D is present in an amount of from 0.25 to 0.5% by weight.
8. A process for producing a molding with a high-gloss, chemical-resistant surface for the exterior area of motor vehicles which comprises utilizing the thermoplastic molding composition according to claim 1 .