Deterministic cleave of optical fiber
View Patent ↗Axial tension is applied to an optical fiber that had been scored at the intended cleave location, wherein the axial tension is applied in a time-varying manner to maintain the stress intensity factor for crack on the fiber within an acceptable level to produce a stable crack growth at a reasonable rate to cleave the fiber without requiring polishing of the end surface. Careful control of the applied tension force with time acts to control the velocity of the propagating crack by maintaining substantially constant stress intensity factor. The applied axial tension force is reduced with time and/or crack growth (as crack propagates). As a result, the strain energy in the fiber material is released by formation of a single plane with an optical quality surface without requiring polishing. A substantially flat optical surface of enhanced optical quality is formed at the cleaved end of the optical fiber.
1. A method of cleaving an optical fiber, comprising:
providing an initial crack at the surface of the optical fiber;
applying an initial force to initiate crack growth from the initial crack; and
after crack growth is initiated, applying an axial force to the optical fiber in a time varying manner, wherein the axial force is applied in a manner decreasing with time, to propagate crack growth to cleave the optical fiber.
2. The method of claim 1 , wherein the axial force is applied in a monotonically decreasing manner.
3. The method of claim 1 , wherein the axial force is applied in a manner decreasing at a rate that decreases with time.
4. The method of claim 2 , wherein the axial force is applied in a manner decreasing with crack growth.
5. The method of claim 4 , wherein the axial force is applied in a manner decreasing at a rate that progressively decreases with crack growth.
6. The method of claim 5 , wherein the axial force is applied to produce a crack growth velocity ranging between 10 −6 and 10 −4 m/s.
7. The method of claim 1 , wherein the axial force is applied to produce a stress intensity factor for crack on the fiber which is maintained substantially constant as the axial force is being reduced.
8. The method of claim 1 , wherein the axial force is applied to produce a stress intensity factor for crack on the fiber which ranges between 0.750 MPa·m 0.5 and 0.35 MPa·m 0.5 .
9. The method of claim 1 , wherein the axial force is applied in a manner to produce a stable crack growth to obtain a cleaved end surface having an optical quality without requiring polishing.
10. The method of claim 9 , wherein the cleave end surface of an optical quality that has a maximum variation of less than 100 nm with respect to a nominal plane, and a surface peak-to-valley roughness that is less than 5 nm.
11. The method of claim 1 , wherein the initial crack is circumferential about the optical fiber.
12. The method of claim 1 , wherein the initial crack is produced without producing sub-surface crack beyond the initial crack.
13. The method of claim 1 , wherein the axial force is applied in tension.
14. A method of cleaving an optical fiber, comprising:
providing an initial crack at the surface of the optical fiber;
applying an initial force to initiate crack growth; and
applying an axial force to the optical fiber in a manner to produce a stable crack growth to obtain a cleaved end surface, wherein the axial force is applied in a time varying manner, and wherein the axial force is applied in a manner decreasing with time.
15. A method of cleaving an optical fiber comprising:
providing an initial crack at the surface of the optical fiber;
applying an initial force to initiate crack growth; and
applying an axial force to the optical fiber in a manner to produce a stable crack growth to obtain a cleaved end surface, wherein the axial force is applied to produce a stress intensity factor for crack on the fiber which is at or below a critical stress intensity factor that produces a stable crack growth.
16. The method of claim 15 , wherein the stress intensity factor ranges between 0.750 MPa·m 0.5 and 0.35 MPa·m 0.5 .
17. The method of claim 14 , wherein the axial force is applied in a manner decreasing with crack growth.
18. The method of claim 14 , wherein the crack growth is at a rate whereby the end surface has an optical quality without requiring polishing.
19. The method of claim 15 , wherein the crack growth is at a rate whereby the end surface has an optical quality without requiring polishing.
20. The method of claim 15 , wherein the axial force is applied in a manner decreasing with time.