Separator including porous coating layer and electrochemical device including the same

1. A separator comprising a planar non-woven fabric substrate having a plurality of pores, and a porous coating layer formed on at least one surface of the non-woven fabric substrate and composed of a mixture of filler particles and a binder polymer, wherein the filler particles comprise inorganic particles and conductive positive temperature coefficient (PTC) particles composed of a mixture of conductive particles and a low melting point resin having a melting point lower than that of the non-woven fabric substrate,

wherein the conductive PTC particles are present in an amount of 1 to 50% by weight, based on the total weight of the filler particles, and

wherein the inorganic particles are present in an amount of 50% by weight or more based on the total weight of the filler particles.

2. The separator according to claim 1 , wherein the conductive particles are made of at least one carbonaceous material selected from the group consisting of natural graphite, artificial graphite, carbon black and graphite.

3. The separator according to claim 1 , wherein the filler particles have an average particle diameter of 0.001 to 10 μm.

4. The separator according to claim 1 , wherein the conductive particles and the low melting point resin are present in a weight ratio of 50:50 to 90:10.

5. The separator according to claim 1 , wherein the low melting point resin has a melting point of 80 to 130° C.

6. The separator according to claim 1 , wherein the low melting point resin is a polyolefin resin.

7. The separator according to claim 1 , wherein the weight ratio of the filler particles to the binder polymer is from 50:50 to 99:1.

8. The separator according to claim 1 , wherein the binder polymer has a solubility parameter of 15 to 45 Mpa 1/2 .

9. The separator according to claim 1 , wherein the binder polymer is selected from the group consisting of polyvinylidene fluoride-co-hexafluoropropylene, polyvinylidene fluoride-co-trichloroethylene, polymethyl methacrylate, polyacrylonitrile, polyvinylpyrrolidone, polyvinyl acetate, polyethylene-co-vinyl acetate, polyethylene oxide, cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate, cyanoethylpullulan, cyanoethyl polyvinyl alcohol, cyanoethyl cellulose, cyanoethyl sucrose, pullulan, carboxymethyl cellulose, and mixtures thereof.

10. The separator according to claim 1 , wherein the non-woven fabric substrate is composed of microfibers having an average diameter of 0.5 to 10 μm.

11. The separator according to claim 10 , wherein the microfibers have a melting point of at least 200° C.

12. The separator according to claim 10 , wherein the non-woven fabric substrate has a pore size distribution in which at least 50% of the pores have a longest diameter of 0.1 to 70 μm.

13. The separator according to claim 10 , wherein the microfibers are composed of at least one polymer selected from the group consisting of polyester, polyacetal, polyamide, polycarbonate, polyimide, polyether ether ketone, polyethersulfone, polyphenylene oxide, polyphenylene sulfide and polyethylene naphthalate.

14. The separator according to claim 1 , wherein the non-woven fabric substrate has a thickness of 9 to 30 μm.

15. The separator according to claim 1 , wherein the porous coating layer is loaded in an amount of 5 to 20 g per square meter (m 2 ) of the non-woven fabric substrate.

16. An electrochemical device comprising a cathode, an anode and the separator according to claim 1 interposed between the cathode and the anode.

17. The electrochemical device according to claim 16 , wherein the electrochemical device is a lithium secondary battery.