Methods for preparing and regenerating materials containing amorphous iron oxide hydroxide and desulfurizer comprising the same
View Patent ↗Methods for preparing a composition containing amorphous iron oxide hydroxide. Methods for regeneration of the amorphous iron oxide hydroxide after it has been used as desulfurizer. Regenerable desulfurizer with high sulfur capacity containing amorphous iron oxide hydroxide, not less than 88% w/w, and organic binder not less than 7% w/w. The organic binder is sodium carboxymethylcellulose, sesbania powder, cellulose powder, or a mixture thereof. A method for preparing the desulfurizer. A method for regenerating the waste agent produced after the desulfurizer and the composition containing the desulfurizer are used as desulfurizer. This method allows the desulfurizer and the composition containing the desulfurizer to be regenerated and reused avoiding the need for landfill disposal and environmental pollution.
1. A method for preparing a composition comprising amorphous iron oxide hydroxide, comprising the following steps:
(1) preparing a ferrous salt solution;
(2) mixing the ferrous salt solution with a carbonate solution, a bicarbonate solution, a carbonate solid, or a bicarbonate solid to form a first mixture, and allowing the first mixture to react to yield a second mixture;
(3) filtering the second mixture to remove generated soluble salt and yield a filter cake, and washing the filter cake with water; and
(4) forming a suspension comprising the filter cake, charging the suspension with a gas comprising oxygen, and then filtering and drying the suspension to yield a composition comprising amorphous iron oxide hydroxide.
2. The method of claim 1 , wherein the carbonate solid is selected from the group consisting of sodium carbonate, ammonium carbonate and potassium carbonate, and the bicarbonate solid is selected from the group consisting of sodium bicarbonate, ammonium bicarbonate and potassium bicarbonate.
3. The method of claim 1 , wherein a pH value of the second mixture is between 7.5 and 8.5.
4. The method of claim 2 , wherein Na + , K + , or NH 4 + constitutes less than 0.5 weight % of the filter cake after the filter cake is washed with water.
5. The method of claim 1 , wherein the filter cake constitutes between 5 weight % and 30 weight % of the suspension.
6. The method of claim 5 , wherein the filter cake constitutes between 10 weight % to 15 weight % of the suspension.
7. The method of claim 1 , wherein the temperature at which the drying of the suspension is carried out does not exceed 100° C.
8. The method of claim 7 , wherein temperature at which the drying of the suspension is carried out is between 80° C. and 100° C.
9. The method of claim 1 , wherein the gas comprising oxygen is air.
10. The method of claim 1 , wherein the suspension is charged with the gas comprising oxygen until the weight proportion of Fe 2 /Fe t is less than 1%.
11. The method of claim 1 , wherein the amorphous iron oxide hydroxide constitutes between 65 weight % and 100 weight % of the composition.