Sintered cubic boron nitride cutting tool
A cutting tool having a sintered compact including 30 to 80 vol. % cubic boron nitride and a binder phase, wherein the binder phase includes about 2 to about 6 vol. % ZrN, is disclosed. In more specific examples, the cutting tool has a sintered compact including 30 to 80 vol. % cubic boron nitride, between about 4 vol. % and about 15 vol. % aluminum and/or aluminum compound and/or aluminum alloy and/or combinations thereof, and a binder phase, wherein the binder phase includes TiN and about 3 to about 5 vol. % ZrN, and wherein the cubic boron nitride has a grain size of less than 20 microns. Cutting tools of the disclosed composition display improved performance, particularly at higher operating speeds, e.g., about 200 m/min or greater.
1. A cutting tool for high-speed hard part turning, comprising:
a sintered compact including about 30 to about 80 vol. % cubic boron nitride and a binder phase,
wherein prior to sintering, the binder phase includes TiN, about 7.5 vol. % Al, and about 3 to about 4.25 vol. % ZrN relative to the entire compact components, and
wherein the binder phase has a higher vol. % of TiN than ZrN.
2. The cutting tool of claim 1 , wherein the binder phase includes about 3 vol. % ZrN.
3. The cutting tool of claim 1 , wherein the aluminum is present as an aluminum alloy that includes NiAl 3 .
4. The cutting tool of claim 1 , wherein the sintered compact includes about 50 vol. % cubic boron nitride relative to the whole sintered compact.
5. The cutting tool of claim 1 , wherein the cubic boron nitride has a grain size of less than about 20 microns.
6. The cutting tool of claim 1 , wherein the TiN and the ZrN are in a ratio from about 4.23 to about 12.58 by vol. %.
7. The cutting tool of claim 1 , wherein the cubic boron nitride has a grain size having a bimodal distribution with about 75% of the cubic boron nitride having a grain size in a first range of about 2 microns to about 3 microns and about 25% of the cubic boron nitride has a grain size in a second range of about 1 micron to about 2 microns.
8. The cutting tool of claim 1 , wherein the TiN and the ZrN are in a ratio greater than 4.23 by vol. %.
9. The cutting tool of claim 1 , wherein high-speed hard part turning occurs at or above about 200 surface meters per minute.
10. A cutting tool for high-speed hard part turning, comprising:
a sintered compact including about 30 to about 80 vol. % cubic boron nitride, about 7.5 vol. % aluminum or an aluminum alloy, and a binder phase,
wherein the binder phase includes about 3 to about 4.5 vol. % ZrN relative to the entire compact components,
wherein the binder phase includes TiN, and
wherein the binder phase has a higher vol. % of TiN than ZrN.
11. The cutting tool of claim 10 , wherein the sintered compact includes about 50 vol. % cubic boron nitride relative to the whole sintered compact.
12. The cutting tool of claim 10 , wherein the cubic boron nitride has a grain size of less than about 20 microns, the grain size having a bimodal distribution with about 75% of the cubic boron nitride having a grain size in a first range of about 2 microns to about 3 microns and about 25% of the cubic boron nitride has a grain size in a second range of about 1 micron to about 2 microns.
13. A cutting tool, comprising:
a sintered compact including about 50 vol. % cubic boron nitride and a binder phase, wherein the binder phase includes TiN, about 7.5 vol. % Al, and about 3 to about 4.25 vol. % ZrN, and
wherein the binder phase has a higher vol. % of TiN than ZrN.