Bent metal member and a method for its manufacture
View Patent ↗A method of manufacturing a bent metal member comprises supporting the outer surface of a tubular metal material having a Zn-Fe alloy coating layer at two locations spaced in the axial direction of the metal material. The metal material is fed in its axial direction and heated at a position between the two locations to a temperature range of at least the Ac 3 point at a heating speed such that the rate of temperature increase is at least 3.0×10 2 ° C. per second, held so that the time for which the surface of the metal material is at a temperature of 8.0×10 2 ° C. or higher is at most 2 seconds, and then rapid cooled. A bending moment is imparted to the healed portion in two or three dimensions to manufacture a bent metal member having on its surface a Zn-based layer which contains an η, phase.
1. A method of manufacturing a bent metal member characterized by
supporting the outer surface of a tubular metal material having on its surface a Zn—Fe alloy coating layer which satisfies the following Condition 1 at two locations spaced in the axial direction of the metal material so that the metal material can move in its axial direction,
feeding the metal material in its axial direction,
heating the metal material at a position between the two locations to a temperature range of at least the Ac 3 point at a heating speed such that the rate of temperature increase is at least 3.0×10 2 ° C. per second, performing holding so that the length of time for which the surface of the metal material is at a temperature of 8.0×10 2 ° C. or higher is at most 2 seconds, and then performing rapid cooling, and
imparting a bending moment to the portion of the metal material which underwent the heating by two-dimensionally or three-dimensionally varying the position of one of the two locations which is located downstream in the feed direction of the metal material,
thereby manufacturing a bent metal member having on its surface a Zn-based layer which contains an η phase and which satisfies the following Condition 2:
Condition 1
Coating weight: 30-90 g/m 2 per side
Fe content: 8-20 mass %
Surface roughness Ra prescribed by JIS B 0601: at most 0.8 μm;
Condition 2
Coating weight: at most 90 g/m 2 per side
Fe content: 8-35 mass %
Surface roughness Ra prescribed by JIS B 0601: at most 2.0 μm.