View Patent ↗The present invention relates generally to the field of catalysts for use in connection with one or more types of emissions control (e.g., emissions control associated with the combustion of one or more types of fossil fuel) and, in particular to catalyst compositions that possess an improved resistance to at least one type of poisoning. In another embodiment, the catalysts of the present invention are designed to be utilized in conjunction with an SCR and possess an improved resistance to phosphorus poisoning.
1. A poison-resistant SCR catalyst composition comprising:
(i) at least one vanadium compound or metal;
(ii) at least one tungsten compound or metal;
(iii) at least one titanium compound or metal; and
(iv) at least one additional compound selected from one or more cobalt compounds or metal, one or more niobium compounds or metal, or mixtures of two or more thereof,
wherein poison-resistance in the SCR catalyst is achieved due to the molar ratio of the metal portion of component (iv) to the metal portion of component (i) falling in the range of about 10:1 to about 1:10.
2. The catalyst composition of claim 1 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 9:1 to about 1:9.
3. The catalyst composition of claim 1 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 8:1 to about 1:8.
4. The catalyst composition of claim 1 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 7:1 to about 1:7.
5. The catalyst composition of claim 1 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 4:1 to about 1:4.
6. The catalyst composition of claim 1 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 3:1 to about 1:3.
7. The catalyst composition of claim 1 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 2:1 to about 1:2.
8. The catalyst composition of claim 1 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is about 2:1.
9. The catalyst composition of claim 1 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (ii) is in the range of about 3:1 to about 1:35.
10. The catalyst composition of claim 1 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (iii) is in the range of about 1:1 to about 1:2000.
11. The catalyst composition of claim 1 , wherein the catalyst composition contains less than about 5 weight percent of one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
12. The catalyst composition of claim 1 , wherein the catalyst composition contains less than about 2.5 weight percent of one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
13. The catalyst composition of claim 1 , wherein the catalyst composition contains less than about 1 weight percent of one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
14. The catalyst composition of claim 1 , wherein the catalyst composition contains less than about 0.5 weight percent of one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
15. The catalyst composition of claim 1 , wherein the catalyst composition is free of any one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
16. The catalyst composition of claim 1 , wherein the catalyst composition has an SO 2 to SO 3 conversion, or oxidation, rate that is about 2 percent or less.
17. The catalyst composition of claim 1 , wherein the catalyst composition is resistant to phosphorus poisoning.
18. A poison-resistant SCR catalyst composition comprising:
(i) at least one vanadium compound or metal;
(ii) at least one tungsten compound or metal;
(iii) at least one titanium compound or metal; and
(iv) at least one additional compound selected from one or more cobalt compounds or metal, one or more niobium compounds or metal, or mixtures of two or more thereof,
wherein poison-resistance in the SCR catalyst is achieved due to: (a) the molar ratio of the metal portion of component (iv) to the metal portion of component (i) falling in the range of about 10:1 to about 1:10; (b) the molar ratio of the metal portion of component (iv) to the metal portion of component (ii) falling in the range of about 3:1 to about 1:35; and (c) the molar ratio of the metal portion of component (iv) to the metal portion of component (iii) falling in the range of about 1:1 to about 1:2000.
19. The catalyst composition of claim 18 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 9:1 to about 1:9.
20. The catalyst composition of claim 18 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 8:1 to about 1:8.
21. The catalyst composition of claim 18 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 7:1 to about 1:7.
22. The catalyst composition of claim 18 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 4:1 to about 1:4.
23. The catalyst composition of claim 18 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 3:1 to about 1:3.
24. The catalyst composition of claim 18 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 2:1 to about 1:2.
25. The catalyst composition of claim 18 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is about 2:1.
26. The catalyst composition of claim 18 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (ii) is in the range of about 2.5:1 to about 1:32.5.
27. The catalyst composition of claim 18 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (iii) is in the range of about 1:1.5 to about 1:1750.
28. The catalyst composition of claim 18 , wherein the catalyst composition contains less than about 5 weight percent of one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
29. The catalyst composition of claim 18 , wherein the catalyst composition contains less than about 2.5 weight percent of one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
30. The catalyst composition of claim 18 , wherein the catalyst composition contains less than about 1 weight percent of one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
31. The catalyst composition of claim 18 , wherein the catalyst composition contains less than about 0.5 weight percent of one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
32. The catalyst composition of claim 18 , wherein the catalyst composition is free of any one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
33. The catalyst composition of claim 18 , wherein the catalyst composition has an SO 2 to SO 3 conversion, or oxidation, rate that is about 2 percent or less.
34. The catalyst composition of claim 18 , wherein the catalyst composition is resistant to phosphorus poisoning.
35. A method for increasing the active life of a catalyst and/or preventing, reducing, mitigating and/or controlling phosphorus poisoning in an SCR catalyst, the method comprising the steps of:
(a) providing at least one SCR catalyst composition, the SCR catalyst composition comprising:
(i) at least one vanadium compound or metal;
(ii) at least one tungsten compound or metal;
(iii) at least one titanium compound or metal; and
(iv) at least one additional compound selected from one or more cobalt compounds or metal, one or more niobium compounds or metal, or mixtures of two or more thereof,
wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 10:1 to about 1:10; and
(b) supplying a NO x -containing gas to the catalyst and at least one other compound to permit the catalyst to control NO x by the conversion of NO x into another nitrogen compound or nitrogen (N 2 ) gas,
wherein the catalyst composition is resistant to phosphorus poisoning due to at least the molar ratio of component (iv) to component (i).
36. The method of claim 35 , wherein the at least one other compound is ammonia and the catalyst composition is an SCR catalyst.
37. The method of claim 35 , wherein the method is applied to combustion, waste or flue gasses of a combustion process selected from a fossil fuel powered mobile, or stationary, combustion process, a biomass combustion process, or a waste combustion process.
38. The method of claim 35 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 9:1 to about 1:9.
39. The method of claim 35 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 8:1 to about 1:8.
40. The method of claim 35 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 7:1 to about 1:7.
41. The method of claim 35 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 4:1 to about 1:4.
42. The method of claim 35 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 3:1 to about 1:3.
43. The method of claim 35 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is in the range of about 2:1 to about 1:2.
44. The method of claim 35 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (i) is about 2:1.
45. The method of claim 35 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (ii) is in the range of about 3:1 to about 1:35.
46. The method of claim 35 , wherein the molar ratio of the metal portion of component (iv) to the metal portion of component (iii) is in the range of about 1:1 to about 1:2000.
47. The method of claim 35 , wherein the catalyst composition contains less than about 5 weight percent of one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
48. The method of claim 35 , wherein the catalyst composition contains less than about 1 weight percent of one or more binary metal oxides, or ternary metal oxides, formed from any suitable combination of one or two of Co and/or Nb in combination with either one or both of V and W.
49. The method of claim 35 , wherein the catalyst composition has an SO 2 to SO 3 conversion, or oxidation, rate that is about 2 percent or less.