Rubber composition and fuel tank packing for automobile using the composition
View Patent ↗Provided is a rubber composition, which is excellent in fuel permeation resistance, and is capable of achieving improvements in low-temperature embrittlement property and solvent crack property. The rubber composition includes: a fluororubber having a fluorine concentration content of 70 to 71 wt % as a main component; a crosslink-type agent; and the following components (A) and (B), in which: the total content [(A)+(B)] of the above-mentioned components (A) and (B) falls within the range of 17 to 25 parts by weight with respect to 100 parts by weight of the above-mentioned fluororubber; and a weight ratio (A)/(B) of the content of the above-mentioned component (A) to the content of the above-mentioned component (B) falls within the range of 2.0/1 to 3.0/1: (A) barium sulfate; and (B) a neutral silica.
1. A rubber composition, comprising:
a fluororubber having a fluorine content of 70 to 71 wt % as a main component;
a crosslinking agent; and
the following components (A) and (B), wherein:
a total content [(A)+(B)] of the component (A) and the component (B) falls within a range of 17 to 25 parts by weight with respect to 100 parts by weight of the fluororubber; and
a weight ratio (A)/(B) of a content of the component (A) to a content of the component (B) falls within a range of 2.0/1 to 3.0/1:
(A) barium sulfate; and
(B) a neutral silica having a pH of 5.0 to 9.0.
2. A rubber composition according to claim 1 , wherein:
the crosslinking agent comprises the following components (C) and (D);
a total content [(B)+(C)+(D)] of the component (B), the component (C), and the component (D) falls within a range of 10 to 14 parts by weight with respect to 100 parts by weight of the fluororubber;
a weight ratio [(B)/((C)+(D))] of the content of the component (B) to a total content [(C)+(D)] of the component (C) and the component (D) falls within a range of 0.9/1 to 1.5/1; and
a weight ratio (C)/(D) of a content of the component (C) to a content of the component (D) falls within a range of 1.8/1 to 2.0/1:
(C) an organic peroxide; and
(D) an isocyanurate compound.
3. A rubber composition according to claim 1 , which is a vulcanized composition.
4. A rubber composition according to claim 2 , which is a vulcanized composition.
5. A rubber composition according to claim 1 , wherein the neutral silica (B) has a pH of 5.5 to 8.5.
6. A rubber composition according to claim 1 ,
wherein a specific surface area of the neutral silica (B) falls within a range of 30 to 350 m 2 /g in conformity with ASTM D 3037-81.
7. A rubber composition according to claim 1 , wherein the barium sulfate (A) has the following properties (I) to (III):
(I) an average particle diameter of 0.01 to 50 μm;
(II) a specific surface area of 0.1 to 150 m 2 /g; and
(III) an oil absorption of 1 to 50 ml/100 g.