View Patent ↗Heat aging of the composition comprising melt-fabricable tetrafluoroethylene/perfluoro(alkyl vinyl ether) copolymer, the alkyl containing 1 to 5 carbon atoms and melt flowable polytetrafluoroethylene is effective to cause thermal transformation of the composition in the solid state, which is epitaxial co-crystallization of the polymer components of the composition, and other valuable changes, such as increased continuous use temperature.
1. Process comprising heat aging a composition comprising melt-fabricable tetrafluoroethylene/perfluoro(alkyl vinyl ether) copolymer, wherein said perfluoroalkyl contains 1 to 5 carbon atoms, and melt flowable polytetrafluoroethylene, said heat aging being carried out at a temperature greater than 260° C. with said composition being in the solid state.
2. The process of claim 1 wherein said heat aging causes said composition to undergo epitaxial co-crystallization.
3. The process of claim 1 wherein said heat aging is at a temperature of at least 280° C. and/or for at least 4 hours.
4. The process of claim 1 wherein said heat aging is at a temperature of at least 300° C.
5. The process of claim 1 wherein said heat aging is effective wherein said composition exhibits a continuous use temperature of at least 300° C.
6. The process of claim 5 wherein the exhibition of said continuous use temperature is characterized by said composition retaining at least 80% of its tensile modulus prior to said heat aging.
7. The process of claim 1 wherein said heat aging is effective to reduce the coefficient of friction of said composition.
8. The process of claim 1 wherein said heat aging is effective to reduce permeation of said composition by one or more of the gases methane, oxygen and carbon dioxide by at least 50%.
9. The process of claim 1 wherein said heat aging is effective to increase the resistance of said composition to sagging and/or ballooning.
10. The process of claim 8 wherein said composition is in the form of tubing.
11. The process of claim 1 wherein said heat aging produces one or more of the following crystallographic changes: (i) increased in crystallinity index by at least 10%, (ii) increase in apparent crystallite size, (iii) improved uniformity in crystal structure characterized by an increase in long period coherence of at least 10%, (iv) increase in thickness of crystalline layer by increase in long period of at least 25%, and (v) apparent crystallite size of at least 280 {acute over (Å)}, crystallinity index of at least 44, long period of at least 375{acute over (Å)}, and long period coherence of at least 450{acute over (Å)}.
12. The process of claim 1 wherein said heat aging is effective wherein said composition exhibits an increase in storage modulus of at least 30% at 300° C.
13. The process of claim 1 wherein said heat aging is effective to decrease the melt flow rate of said composition by at least 25%.