View Patent ↗A method of making frac sand having a selected grade from a naturally occurring, mined sand having a SiO 2 content of at least about 80 percent and having a particle size range where the maximum particle size is less than about 8.0 mm, comprising: crushing the mined sand into an intermediate particulate material; screening the particulate material into a feedstock with particles having a particle size coarser than about 350 mesh and initial values for roundness and sphericity of the particles; passing the particles of the feedstock through a blast tube with an outlet to pneumatically abrade the particles and propel the feedstock in a stream under a given pressure from the outlet; directing the pressurized stream against a fixed target located at a given distance from said outlet to physically abrade the particles to form an output mass containing abraded particles: and, repeating operations (c) and (d) a number of times or process stages until the particles resulting from the repeatedly abraded output mass is a final output mass having both processed roundness and sphericity values of at least 0.6 and wherein the values are greater than the initial values of the feedstock by at least about 0.10 to 0.50.
1. A method of making a proppant from a naturally occurring, mined granular mineral having a hardness over 6.0 Mohs, said method comprising:
(a) converting said granular mineral into a feedstock of particles having a maximum particle size and a given sphericity;
(b) subjecting said feedstock to a high velocity mechanical action to increase the sphericity of the particles of said feedstock;
(c) continuing said high velocity mechanical operation for a time to convert said given sphericity of said particles of said feedstock into a proppant with a processed sphericity greater than 0.60.
2. The method as defined in claim 1 wherein said high velocity mechanical action includes abrading said particles by particle-to-particle contact.
3. The method as defined in claim 2 wherein said high velocity mechanical action includes impinging said particles at high velocity against a metal member.
4. The method as defined in claim 3 wherein said metal member is fixed.
5. The method as defined in claim 2 wherein said processed sphericity is greater than about 0.80.
6. The method as defined in claim 2 wherein said proppant is frac sand and said mineral is silica sand.
7. The method as defined in claim 6 wherein said silica sand has at least 80% SO 2 .
8. The method as defined in claim 2 including:
(d) screening said proppant into a selected grade.
9. The method as defined in claim 1 wherein said high velocity mechanical action includes impinging said particles at high velocity against a metal member.
10. The method as defined in claim 9 wherein said metal member is fixed.
11. The method as defined in claim 1 wherein said processed sphericity is greater than about 0.80.
12. The method as defined in claim 1 wherein said proppant is frac sand and said mineral is silica sand.
13. The method as defined in claim 12 wherein said silica sand has at least 80% S 1 O 2 .
14. The method as defined in claim 1 including:
(d) screening said proppant into a selected grade.
15. The method as defined in claim 14 wherein said selected grade has a maximum size of 6-35 mesh and a minimum size of 20-140 mesh.
16. The method as defined in claim 14 wherein said selected grade has a maximum size in the range of 12-20 mesh and a minimum size in the range of 30-50 mesh.
17. The method as defined in claim 1 wherein said high velocity mechanical action involves moving said feedstock at a high velocity.
18. The method as defined in claim 17 wherein said high velocity mechanical action includes impinging said particles at high velocity against a metal member.
19. The method as defined in claim 18 wherein said processed sphericity is greater than about 0.80.
20. The method as defined in claim 18 wherein said proppant is frac sand and said mineral is silica sand.
21. The method as defined in claim 20 wherein said silica sand has at least 80% S 1 O 2 .
22. The method as defined in claim 18 wherein said metal member is fixed.
23. The method as defined in claim 17 wherein said processed sphericity is greater than about 0.80.
24. The method as defined in claim 17 wherein said proppant is frac sand and said mineral is silica sand.
25. The method as defined in claim 24 wherein said silica sand has at least 80% S 1 O 2 .
26. The method as defined in claim 17 including:
(d) screening said proppant into a selected grade.
27. The method as defined in claim 1 wherein said mineral is naturally occurring olivine.