Polyolefin masterbatch and composition suitable for injection molding
A masterbatch composition comprising: 70-90% wt of a component (A) being a propylene homopolymer or copolymer of propylene with ethylene or C 4 -C 10 alpha olefins, having a MFR A according to ISO 1133 (230° C./2.16 Kg) ranging from 15 to 70 g/10 min; and 10-30% wt of a component B) being a propylene-ethylene copolymer comprising 25-45% wt of ethylene derived units and having a value of the intrinsic viscosity [η] of the fraction soluble in xylene at room temperature ranging from 5 to 9 dl/g, said masterbatch composition having a total MFR higher than 4 g/10 min, and a value of the flexural modulus measured according to ISO method 178 ranging from 950 to 2000 MPa.
1. A masterbatch composition comprising:
(A) 74-86 wt. %, based upon the total weight of the masterbatch composition, of a component (A) being a propylene homopolymer or a copolymer of propylene with ethylene or C 4 -C 10 alpha olefins, having a polydispersity index from 5 to 10, and an MFR A according to ISO 1133 (230° C./2.16 kg) ranging from 20 to 60 g/10 min; and
(B) 14-26 wt. %, based upon the total weight of the masterbatch composition, of a component (B) being a propylene-ethylene copolymer comprising 30-42 wt. %, based upon the total weight of the propylene-ethylene copolymer, of ethylene derived units and having a value of the intrinsic viscosity [η] of the fraction soluble in xylene at room temperature ranging from 5 to 9 dl/g,
said masterbatch composition having a total MFR from 5.9 to 9.7 g/10 min, an Izod impact resistance at 23° C. ranging from 8.4 to 12.6 kJ/m 2 , an Izod impact resistance at 0° C. ranging from 4.2 to 5.2 kJ/m 2 , a value of the flexural modulus measured according to ISO method 178 ranging from 1100 to 1450 MPa and an elongation at break value measured according to ISO method 527 ranging from 730 to 765%.
2. The masterbatch composition of claim 1 wherein the intrinsic viscosity [η] of the component (B) ranges from 6.5 to 8 dl/g.
3. A thermoplastic polyolefin composition comprising the masterbatch composition of claim 1 .
4. Articles comprising the thermoplastic polyolefin composition of claim 3 .