Golf ball cover material and golf ball using the same
View Patent ↗An object of the present invention is to provide a golf ball which has an increased dry spin rate and wet spin rate on approach shots without sacrificing the processability into the cover. The present invention provides a golf ball cover material having shear loss moduli G1″ (Pa), G2″ (Pa), and G3″ (Pa) that satisfy following equations when measured using a dynamic viscoelasticity measuring apparatus at following conditions. log G1″≦7.09 (1) log G2″≧7.17 (2) log G3″≦7.14 (3) G1″ measuring conditions: shear mode, oscillation frequency: 10 Hz, temperature: 0° C., strain: 0.05%; G2″ measuring conditions: shear mode, oscillation frequency: 10 Hz, temperature: −30° C., strain: 0.05%; and G3″ measuring conditions: shear mode, oscillation frequency: 10 Hz, temperature: 0° C., strain: 5%.
1. A golf ball cover material comprising polyurethane as a resin component,
wherein the polyurethane has a polyol component with a number average molecular weight ranging from 650 to 1,700 as a constituent, and the golf ball cover material has shear loss moduli G1″ (Pa), G2″ (Pa), and G3″ (Pa) that satisfy following equations when measured using a dynamic viscoelasticity measuring apparatus at following conditions:
log G1″≦7.09 (1)
log G2″≧7.17 (2)
log G3″≦7.14 (3)
G1″ measuring conditions: shear mode, oscillation frequency: 10 Hz, temperature: 0° C., strain: 0.05%;
G2″ measuring conditions: shear mode, oscillation frequency: 10 Hz, temperature: −30° C., strain: 0.05%; and
G3″ measuring conditions: shear mode, oscillation frequency: 10 Hz, temperature: 0° C., strain: 5%.
2. The golf ball cover material according to claim 1 , wherein log G3″ ranges from 6.00 to 7.09.
3. The golf ball cover material according to claim 1 , wherein the polyurethane has polytetramethylene ether glycol as a polyol component.
4. The golf ball cover material according to claim 1 , wherein the polyurethane has dicyclohexylmethane diisocyanate as a polyisocyanate component.
5. The golf ball cover material according to claim 1 , wherein the polyurethane has a chain extender having a molecular weight ranging from 30 to 400.
6. The golf ball cover material according to claim 1 , wherein the polyurethane has 1,4-butane diol as a chain extender component.
7. The golf ball cover material according to claim 1 , wherein the golf ball cover material has JIS-A hardness of 74 or more.
8. A golf ball comprising a core and a cover covering the core, wherein the cover is formed from a golf ball cover material comprising polyurethane as a resin component,
wherein the polyurethane has a polyol component with a number average molecular weight ranging from 650 to 1,700 as a constituent, and the golf ball cover material has shear loss moduli G1″ (Pa), G2″ (Pa), and G3″ (Pa) that satisfy following equations when measured using a dynamic viscoelasticity measuring apparatus at following conditions:
log G1″≦7.09 (1)
log G2″≧7.17 (2)
log G3″≦7.14 (3)
G1″ measuring conditions: shear mode, oscillation frequency: 10 Hz, temperature: 0° C., strain: 0.05%;
G2″ measuring conditions: shear mode, oscillation frequency: 10 Hz, temperature: −30° C., strain: 0.05%; and
G3″ measuring conditions: shear mode, oscillation frequency: 10 Hz, temperature: 0° C., strain: 5%.
9. The golf ball according to claim 8 , wherein log G3″ ranges from 6.00 to 7.09.
10. The golf ball according to claim 8 , wherein the polyurethane has polytetramethylene ether glycol as a polyol component.
11. The golf ball according to claim 8 , wherein the polyurethane has dicyclohexylmethane diisocyanate as a polyisocyanate component.
12. The golf ball according to claim 8 , wherein the polyurethane has a chain extender having a molecular weight ranging from 30 to 400.
13. The golf ball according to claim 8 , wherein the polyurethane has 1,4-butane diol as a chain extender component.
14. The golf ball according to claim 8 , wherein the cover has a thickness ranging from 0.3 mm to 2.0 mm.
15. The golf ball according to claim 8 , wherein the cover material has JIS-A hardness of 74 or more.
16. The golf ball according to claim 8 , wherein the core has a compression deformation amount of 2.40 mm or more and 3.20 mm or less, when applying a load from 98 N as an initial load to 1275N as a final load to the core.