Catalyst for polyester polycondensation and method for producing polyester resin using the same
View Patent ↗The invention provides: a polycondensation catalyst for polyester production, which contains titanium atoms, alkaline earth metal atoms and phosphorus atoms, has high reactivity and excellent long-term storage stability, can be easily produced industrially, and has an advantage in cost; a polyester resin obtained with the catalyst; and a molded article. These are: a polymerization catalyst for polyester production containing titanium atoms, alkaline earth metal atoms and phosphorus atoms and having a specific constitution; a polyester resin obtained with the catalyst; and a molded article.
1. A process for producing a liquid polycondensation catalyst comprising titanium, an alkaline earth metal and phosphorus, said process comprising:
(i) mixing an alcohol, an alkaline earth metal compound and an acid phosphoric ester compound to obtain a mixture solution; and
(ii) mixing a titanium compound with the mixture solution obtained in (i);
wherein the acid phosphoric ester compound is a diester of formula (I)
wherein R and R′ each independently represent an alkyl group having 1-6 carbon atoms, a cycloalkyl group, an aryl group or a 2-hydroxyethyl group.
2. The process according to claim 1 , wherein the liquid polycondensation catalyst contains water is an amount of 0.01 to 10% by weight.
3. The process according to claim 1 , wherein the titanium content of the liquid polycondensation catalyst, in terms of titanium atom content, is 0.01 to 2.0% by weight, and the molar ratio of alkaline earth metal to phosphorous and the molar ratio of titanium to phosphorous satisfy expressions (1) and (2) respectively:
0.1 ≦M/P≦ 3 (1)
0.1≦Ti/ P≦ 5 (2)
wherein Ti, M and P each respectively represent the content, on mole basis, of titanium, alkaline earth metal, and phosphorous in the liquid polycondensation catalyst.
4. The process according to claim 1 , wherein the alkaline earth metal compound is a magnesium compound.
5. The process according to claim 4 , wherein the magnesium compound is a magnesium salt of an organic acid, or a hydrate of the salt.
6. The process according to claim 1 , wherein the titanium compound is a tetraalkyl titanate.
7. The process according to claim 1 , wherein the alcohol is a monohydric alcohol or an alkylene glycol.