Wrought and cast aluminum alloy with improved resistance to mechanical property degradation
View Patent ↗Aluminum-based alloys for casting or wrought processing having improved combinations of properties, including improved high temperature strength, are provided. The alloys generally comprise copper, magnesium, silver, and titanium, along with scandium and/or cobalt. Zirconium, zinc, and/or vanadium may also optionally be present in the alloy. When cobalt is present in the alloy, nickel may also optionally be present. Cast and wrought products, as well as methods of making the same using the alloys, are also disclosed.
1. An aluminum-based alloy comprising:
4 to 6% by weight Cu;
0.2 to 1% by weight Mg;
0.1 to 1.5% by weight Ag;
0.15 to 0.35% by weight Ti;
0.25 to 1.5% by weight Co;
0.05 to 1% by weight Zn;
less than 0.05% by weight Mn;
optionally 0.1 to 0.2% by weight Zr; and
balance aluminum and incidental elements and impurities, said % by weight being based upon the total weight of the alloy taken as 100% by weight, wherein said alloy is substantially free of Si.
2. The alloy of claim 1 , wherein said alloy is substantially free of an element selected from the group consisting of Fe, Mo, Li, Cr, and Rare Earth Elements other than Scandium.
3. The alloy of claim 1 , further comprising up to about 0.1% by weight V.
4. The alloy of claim 1 , further comprising Ni, wherein the ratio of Co:Ni is greater than about 2:1.
5. The alloy of claim 1 , said alloy comprising up to 0.05% by weight of each incidental element or impurity, wherein the total incidental element or impurity content is up to 0.15% by weight, based upon the total weight of the alloy taken as 100% by weight.
6. The alloy of claim 1 , wherein the ratio of Mg:Zn is greater than about 0.5:1.
7. The alloy of claim 1 , said alloy comprising less than about 0.005% by weight Si, based upon the total weight of the alloy taken as 100% by weight.
8. The alloy of claim 1 , wherein Zr is present in said alloy in an amount of from about 0.1 to about 0.2% by weight.
9. A wrought or cast product formed from an aluminum-based alloy comprising:
greater than 4% by weight Cu;
less than 1% by weight Mg, wherein Cu+Mg is from about 4.5 to about 6.75% by weight;
0.1 to 1.5% by weight Ag;
0.15 to 0.35% by weight Ti;
0.25 to 1.5% by weight Co;
0.05 to 1% by weight Zn;
less than 0.05% by weight Mn;
optionally 0.1 to 0.2% by weight Zr; and
balance aluminum and incidental elements and impurities, said % by weight being based upon the total weight of the alloy taken as 100% by weight, wherein said alloy is substantially free of Si.
10. The wrought or cast product of claim 9 , wherein said product is a casting selected from the group consisting of ingot, billet, automobile engines, aircraft engines, marine engines, engine components, appliance parts, tools, automotive wheels, aircraft wheels, pistons, engine blocks, and high performance automobile racing components.
11. The casting of claim 10 , wherein said casting is a Grade A casting.
12. The wrought or cast product of claim 9 , wherein said product is a casting, said casting when heated to a temperature of about 400° F. for 100 hours and permitted to return to ambient temperature, having a UTS at ambient temperature of greater than about 55 ksi when formed into a 1″×1″×24″ square rod, when tested according to ASTM E8.
13. The wrought or cast product of claim 9 , wherein said product is a casting, said casting, when formed into a 1″×1″×24″ square rod, having a % elongation of greater than about 6.5%, when tested according to ASTM E8.
14. The wrought or cast product of claim 9 , wherein said product is a wrought product selected from the group consisting of plates, sheets, aerospace engine components, aerospace fuel tanks, aerospace structural components, aerospace containers, airplane wheels, aircraft thrust reversers, aircraft nacelle inlet structures, aircraft underwing components, automobile connecting rods, crankshafts, wheel spindles, axle beams, pistons, gears, wheels, steering arms, and forged automobile racing engines.
15. The wrought or cast product of claim 9 , wherein said product is a wrought product, said product having an initial UTS, and wherein said wrought product when heated to 450° F. for 200 hours and permitted to return to ambient temperature has a subsequent UTS that is no less than about 85% of said initial UTS, when tested according to ASTM E8.
16. The wrought or cast product of claim 9 , wherein said product is a wrought product, said wrought product when heated to a temperature of about 450° F. for 200 hours and permitted to return to ambient temperature, having a subsequent Rockwell Hardness of greater than about 35 at ambient temperature, when tested according to ASTM E18.
17. A cast aluminum alloy product comprising:
greater than 4% by weight Cu;
less than 1% by weight Mg, wherein Cu+Mg is from about 4.5 to about 6.75% by weight;
0.1 to 1.5% by weight Ag;
0.15 to 0.35% by weight Ti;
0.25 to 1.5% by weight Co;
0.05 to 1% by weight Zn;
less than 0.05% by weight Mn;
optionally 0.1 to 0.2% by weight Zr;
0.05 to 1% by weight Sc; and
balance aluminum and incidental elements and impurities, wherein the percentages by weight are based upon the total weight of the alloy taken as 100% by weight, said alloy being substantially free of Si.
18. A method of making a cast aluminum alloy product, said method comprising:
(a) providing an alloy in molten form comprising:
greater than 4% by weight Cu;
less than 1% by weight Mg, wherein Cu+Mg is from about 4.5 to about 6.75% by weight;
0.1 to 1.5% by weight Ag;
0.15 to 0.35% by weight Ti;
0.25 to 1.5% by weight Co;
0.05 to 1% by weight Zn;
less than 0.05% by weight Mn;
optionally 0.1 to 0.2% by weight Zr; and
balance aluminum and incidental elements and impurities, said % by weight being based upon the total weight of the alloy taken as 100% by weight, wherein said alloy is substantially free of Si;
(b) pouring said alloy into a casting mold; and
(c) allowing said alloy to solidify to yield said cast aluminum alloy product.
19. The method of claim 18 , further comprising:
(d) separating said cast aluminum alloy product from said mold; and
(e) subjecting said cast aluminum alloy product to heat treatment.
20. The method of claim 18 , wherein said cast aluminum alloy product requires no reworking.
21. A wrought aluminum alloy product comprising:
greater than 4% by weight Cu;
0.2 to 1% by weight Mg, wherein Cu+Mg is from about 4.5 to about 6.75% by weight;
0.1 to 1.5% by weight Ag;
0.15 to 0.35% by weight Ti;
optionally 0.1 to 0.2% by weight Zr;
0.25 to 1.5% by weight Co;
0.05 to 1% by weight Zn;
less than 0.05% by weight Mn; and
balance consisting essentially of aluminum and incidental elements and impurities, wherein the percentages by weight are based upon the total weight of the alloy taken as 100% by weight, said alloy being substantially free of Si.
22. The wrought aluminum alloy product of claim 21 , said alloy comprising less than about 0.005% by weight Si, based upon the total weight of the alloy taken as 100% by weight.
23. The wrought aluminum alloy product of claim 21 , wherein Zr is present in said alloy in an amount of from about 0.1 to about 0.2% by weight.
24. A method of forming a wrought aluminum alloy product, said method comprising:
(a) providing a casting of an alloy comprising:
greater than 4% by weight Cu;
0.2 to 1% by weight Mg, wherein Cu+Mg is from about 4.5 to about 6.75% by weight;
0.1 to 1.5% by weight Ag;
0.15 to 0.35% by weight Ti;
0.25 to 1.5% by weight Co;
0.05 to 1% by weight Zn;
less than 0.05% by weight Mn;
optionally 0.1 to 0.2% by weight Zr; and
balance aluminum and incidental elements and impurities, said % by weight being based upon the total weight of the alloy taken as 100% by weight, wherein said alloy is substantially free of Si; and
(b) shaping said casting by a process selected from the group consisting of forging, extruding, rolling, pressing, stamping, straightening, stretching, squeezing, bending, drawing, shearing, compression stress relief, shot-peening, peen-forming, and combinations thereof to yield said wrought aluminum alloy product.
25. The method of claim 24 , further comprising subjecting said wrought aluminum alloy product to heat treatment before, after, or before and after said shaping (b).
26. An aerospace structural component formed from an aluminum alloy comprising:
greater than 4% by weight Cu;
0.2 to 1% by weight Mg, wherein Cu+Mg is from about 4.5 to about 6.75% by weight;
0.1 to 1.5% by weight Ag;
0.15 to 0.35% by weight Ti;
optionally 0.1 to 0.2% by weight Zr;
0.25 to 1.5% by weight Co;
0.05 to 1% by weight Zn;
less than 0.05% by weight Mn; and
balance aluminum and incidental elements and impurities, wherein the percentages by weight are based upon the total weight of the alloy taken as 100% by weight, said alloy being substantially free of Si.