Preparation of nitrogen-doped carbon tubes
View Patent ↗A method for synthesizing nitrogen-doped carbon tubes involves preparing a solution of cyanamide and a suitable transition metal-containing salt in a solvent, evaporating the solvent to form a solid, and pyrolyzing the solid under an inert atmosphere under conditions suitable for the production of nitrogen-doped carbon tubes from the solid. Pyrolyzing for a shorter period of time followed by rapid cooling resulted in a tubes with a narrower average diameter.
1. A method for synthesizing nitrogen-doped carbon tubes comprising:
preparing a solution comprising aminomethanenitrile (NCNH 2 ) and a suitable transition metal-containing salt in a solvent to form a transition metal complex,
evaporating the solvent to form a solid, and
pyrolyzing the solid under an inert atmosphere under conditions suitable for the production of nitrogen-doped carbon tubes from the solid wherein the step of pyrolyzing the solid comprises heating the solid from about 850 degrees Celsius to about 1050 degrees Celsius.
2. The method of claim 1 , wherein the step of preparing a solution comprises combining aminomethanenitrile (NCNH 2 ) and a suitable transition-metal-containing salt in a solvent and heating to form a solution.
3. The method of claim 1 , wherein the suitable transition metal-containing salt comprises a metal selected from cobalt, nickel, iron, or mixtures thereof.
4. The method of claim 1 , wherein the suitable transition metal-containing salt is selected from cobalt carboxylate, nickel carboxylate, iron carboxylate, and mixtures thereof.
5. The method of claim 1 , wherein the step of pyrolyzing the solid comprises heating the solid at 950 degrees Celsius.
6. The method of claim 1 , wherein the solvent comprises an alcohol.
7. The method of claim 5 , wherein the solvent comprises ethanol.
8. The method of claim 1 , wherein the solvent comprises water.
9. The method of claim 5 , wherein the solid is heated for three minutes and then cooled rapidly.
10. The method of claim 9 , wherein the nitrogen-doped carbon tubes are nanotubes.
11. The method of claim 1 , wherein the nitrogen-doped tubes include microtubes.