One-component moisture curing adhesive for use in vehicle lighting appliance and vehicle lighting appliance using the same
A one-component moisture curing adhesive for use in a vehicle lighting appliance including: 100 parts by weight of a bifunctional polyether polyol (A) having a molecular weight of not less than 3,000; from 80 to 40 parts by weight of a crystalline polyester polyol (B); from 20 to 60 parts by weight of a non-crystalline polyester polyol (C); a polyisocyanate (D); and a curing catalyst (E), wherein a content of the polyisocyanate (D) is such that a number of isocyanate groups included in the polyisocyanate (D) with respect to a total number of hydroxy groups included in the bifunctional polyether polyol (A), the crystalline polyester polyol (B), and the non-crystalline polyester polyol (C) satisfies NCO/OH=1.2 to 1.5; and a vehicle lighting appliance formed by adhering a lens and a housing the one-component moisture curing adhesive for use in a vehicle lighting appliance.
1. A one-component moisture curing adhesive for use in a vehicle lighting appliance comprising: 100 parts by weight of a bifunctional polyether polyol (A) having a molecular weight of not less than 3,000;
from 80 to 40 parts by weight of a crystalline polyester polyol (B) per 100 parts by weight of the bifunctional polyether polyol (A);
from 20 to 60 parts by weight of a non-crystalline polyester polyol (C) per 100 parts by weight of the bifunctional polyether polyol (A), wherein the non-crystalline polyester polyol (C) is formed from pthalic acid and neopentyl glycol;
a polyisocyanate (D); and
a curing catalyst (E), wherein
a content of the polyisocyanate (D) is such that a number of isocyanate groups included in the polyisocyanate (D) with respect to a total number of hydroxy groups included in the bifunctional polyether polyol (A), the crystalline polyester polyol (B), and the non-crystalline polyester polyol (C) satisfies NCO/OH=1.2 to 1.5.
2. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein a content of the curing catalyst (E) is from 0.05 to 0.5 wt % with respect to a total of the parts by weight of the bifunctional polyether polyol (A), the crystalline polyester polyol (B), the non-crystalline polyester polyol (C), and the polyisocyanate (D).
3. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein a total content of the crystalline polyester polyol (B) and the non-crystalline polyester polyol (C) is from 80 to 120 parts by weight per 100 parts by weight of the bifunctional polyether polyol (A).
4. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein a melt viscosity at 120° C. is not less than 10,000 mPa·s.
5. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein the polyisocyanate (D) is 4,4′-diphenylmethane diisocyanate.
6. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein the curing catalyst (E) is 2,2′-dimorpholino diethyl ether.
7. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein the bifunctional polyether polyol (A) is a polypropylene glycol.
8. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein the bifunctional polyether polyol (A) has a molecular weight of from 3,000 to 4,000.
9. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein the crystalline polyester polyol (B) is formed from sebacic acid and hexanediol.
10. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein the crystalline polyester polyol (B) comprises two hydroxy groups.
11. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , comprising from 60 to 40 parts by weight of a crystalline polyester polyol (B) per 100 parts by weight of the bifunctional polyether polyol (A).
12. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , comprising from 40 to 60 parts by weight of the non-crystalline polyester polyol (C) per 100 parts by weight of the bifunctional polyether polyol (A).
13. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein a total content of the crystalline polyester polyol (B) and the non-crystalline polyester polyol (C) is from 80 to 100 parts by weight per 100 parts by weight of the bifunctional polyether polyol (A).
14. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein the polyisocyanate (D) is an aromatic polyisocyanate.
15. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein the content of the polyisocyanate (D) is such that a number of isocyanate groups included in the polyisocyanate (D) with respect to a total number of hydroxy groups included in the bifunctional polyether polyol (A), the crystalline polyester polyol (B), and the non-crystalline polyester polyol (C) satisfies NCO/OH=1.2 to 1.3.
16. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein a content of the curing catalyst (E) is from 0.1 to 0.3 wt % with respect to a total of the parts by weight of the bifunctional polyether polyol (A), the crystalline polyester polyol (B), the non-crystalline polyester polyol (C), and the polyisocyanate (D).
17. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein a melt viscosity of the adhesive at 120° C. is from 20,000 to 50,000 mPa·s.
18. The one-component moisture curing adhesive for use in a vehicle lighting appliance according to claim 1 , wherein an adhesive strength at a temperature of 80° C. is at least 115 N after curing conditions of 20° C. at 55% RH for 21 days, and a curing depth is at least 4.1 mm as measured from a surface of the adhesive after curing conditions of 20° C. at 55% RH for 7 days.
19. A vehicle lighting appliance formed by adhering a lens and a housing the one-component moisture curing adhesive for use in a vehicle lighting appliance described in claim 1 .
20. The vehicle lighting appliance of claim 19 , wherein the housing is a plasma treated housing comprising polypropylene.