Nanowire fabrication
View Patent ↗Techniques for making nanowires with a desired diameter are provided. The nanowires can be grown from catalytic nanoparticles, wherein the nanowires can have substantially same diameter as the catalytic nanoparticles. Since the size or the diameter of the catalytic nanoparticles can be controlled in production of the nanoparticles, the diameter of the nanowires can be subsequently controlled as well. The catalytic nanoparticles are melted and provided with a gaseous precursor of the nanowires. When supersaturation of the catalytic nanoparticles with the gaseous precursor is reached, the gaseous precursor starts to solidify and form nanowires. The nanowires are separate from each other and not bind with each other to form a plurality of nanowires having the substantially uniform diameter.
1. A product comprising a nanostructure, wherein said nanostructure comprises:
a substrate;
a nanocapsule in contact with the substrate;
a catalytic particle partially embedded within the nanocapsule, wherein the catalytic particle has an exposed surface that is not covered by the nanocapsule; and
a nanowire attached to at least a portion of the exposed surface of the catalytic particle.
2. The nanostructure of claim 1 , wherein the nanoparticle has a diameter in a range from about 1 nm to about 100 nm.
3. The nanostructure of claim 1 , wherein the nanowire has a diameter in a range from about 1 nm to about 100 nm.
4. The nanostructure of claim 1 , wherein a diameter of the nanowire is about the same as a diameter of the catalytic nanoparticle.
5. The nanostructure of claim 1 , wherein the nanocapsule has a thickness in a range from about 5 nm to about 100 nm.
6. The nanostructure of claim 1 , wherein the catalytic nanoparticle comprises one or more of Au, Ag, alloy metal, or Fe.
7. The nanostructure of claim 1 , wherein the nanocapsule comprises one or more of SiO 2 or carbon.
8. The nanostructure of claim 1 , wherein the nanowire comprises one or more of elemental metal, carbon, or Si.
9. The nanostructure of claim 1 , wherein the nanowire extends in a direction generally perpendicular to the generally planar surface.
10. A product comprising a plurality of nanowire structures on a substrate, wherein each of the plurality of nanowire structures comprises:
a nanocapsule in contact with the substrate;
a catalytic particle partially embedded within the nanocapsule, wherein the catalytic particle has an exposed surface that is not covered by the nanocapsule; and
a nanowire attached to at least a portion of the exposed surface of the catalytic particle.
11. The product of claim 10 , wherein a standard deviation of diameters for the nanowires in the plurality of nanowire structures is in a range from about 1% to about 20%.
12. The nanostructure of claim 10 , wherein the catalytic particle protrudes from the second portion of the nanocapsule.