Melt spinning blends of UHMWPE and HDPE and fibers made therefrom
View Patent ↗Compositions that are intimate blends of ultrahigh molecular weight polyethylene and high-density polyethylene (HDPE), and which are melt spinnable. The compositions include certain quasi-spherical particles. Also disclosed is a method of melt spinning from such compositions and the multi-filament fibers produced thereby. The fibers of the invention are useful in a variety of applications.
1. A polyethylene melt spinning composition comprising an intimate blend of:
I) a polyethylene portion comprising:
a) about 50 to about 90 percent by weight of an ultra-high molecular weight polyethylene (UHMWPE) having an intrinsic viscosity of from about 6 to about 15 dl/g; and
b) about 10 to about 50 percent by weight of a high density polyethylene (HDPE) having an intrinsic viscosity of from about 0.75 to about 3 dl/g, and
II) about 0.1 to about 1 percent by weight of a material comprising quasi-spherical particles having a weight average particle size of from about 0.05 to about 10 micrometers and a Mohs' hardness of at least about 4, said particles comprising at least 50 percent by weight of inorganic non-metallic materials;
wherein the polyethylene portion of said blend has an intrinsic viscosity of from about 2.4 to about 5 dl/g and a ratio of weight average to number average molecular weight of at least about 7, with all said intrinsic viscosities being measured in decalin at 135° C. by ASTM D1601-99.
2. The composition of claim 1 , wherein said UHMWPE has an intrinsic viscosity of from about 6 to about 12 dl/g.
3. The composition of claim 1 , wherein the polyethylene portion of said blend has ratio of weight average to number average molecular weight at least about 10.
4. The composition of claim 1 , wherein said particles comprise titanium dioxide.
5. The composition of claim 4 , wherein said titanium dioxide is in the anatase crystalline form.
6. A polyethylene melt spinning composition comprising an intimate blend of:
I) a polyethylene portion comprising:
a) about 50 to about 90 percent by weight of an ultra-high molecular weight polyethylene (UHMWPE) having an intrinsic viscosity of from about 6 to about 15 dl/g; and
b) about 10 to about 50 percent by weight of a high density polyethylene (HDPE) having an intrinsic viscosity of from about 0.75 to about 3 dl/g, and
II) about 0.1 to about 1 percent by weight of a material comprising titanium dioxide in anatase crystalline form having a weight average particle size of from about 0.05 to about 10 micrometers and a Mohs' hardness of at least about 4;
wherein the polyethylene portion of said blend has an intrinsic viscosity of from about 2.4 to about 5 dl/g and a ratio of weight average to number average molecular weight of at least about 7, with all said intrinsic viscosities being measured in decalin at 135° C. by ASTM D1601-99.
7. The composition of claim 6 , wherein said UHMWPE has an intrinsic viscosity of from about 6 to about 12 dl/g.
8. The composition of claim 6 , wherein the ratio of weight average to number average molecular weight at least about 10.