Method of manufacturing a metal matrix composite
View Patent ↗A method of forming a metal matrix composite (MMC),such as a brake drum, by impregnating a preform, which is formed of ceramic particles and ceramic fibers, with a support element, such as a metal. The MMC has a wear surface defined by both the preform and the support element.
1. A method of forming a brake drum for a vehicle by impregnating a preform with a metal with the preform having an inner surface and an opposing outer surface and formed from a composition having ceramic particles and ceramic fibers utilizing a mold having a cavity, said method comprising the steps of:
mixing the composition;
shaping the composition into a cylindrical configuration after the composition has been mixed to define the preform having a continuous inner surface;
positioning the preform within a portion of the cavity of the mold;
heating the metal to form a molten metal;
injecting the molten metal into the cavity of the mold adjacent the outer surface of the preform under pressure;
infiltrating the preform with the molten metal through the outer surface to the inner surface of the preform; and
cooling the molten metal to solidify the molten metal and define the brake drum having a wear surface formed of the infiltrated inner surface with exposed metal, ceramic particles and ceramic fibers.
2. The method as set forth in claim 1 wherein the step of cooling the molten metal to below the melting point is further defined as cooling the molten metal to below the melting point to solidify the molten metal and produce the metal that impregnates the preform to define the brake drum having the wear surface with the preform present on the wear surface in an amount of from about 10 to 60% based on a surface area of the wear surface.
3. The method as set forth in claim 1 wherein the step of cooling the molten metal to below the melting point is further defined as cooling the molten metal to below the melting point to solidify the molten metal and produce the metal that impregnates the preform to define the brake drum having the wear surface with the preform present on the wear surface in an amount of from about 32 to 38% based on a surface area of the wear surface.
4. The method as set forth in claim 1 further including the step of machining the wear surface of the brake drum to a final configuration.
5. The method as set forth in claim 1 further including the step of substantially randomly orienting the ceramic fibers of the composition in three dimensions as the composition is mixed.
6. The method as set forth in claim 5 wherein the step of substantially randomly orienting the ceramic fibers in three dimensions is further defined as randomly orienting greater than 90 out of 100 ceramic fibers in three dimensions as the composition is mixed.
7. The method as set forth in claim 1 further including the step of drying the preform to remove water from the preform.
8. The method as set forth in claim 1 further including the step of baking the preform to remove organic binders and fillers from the preform.
9. The method as set forth in claim 1 further including the steps of heating the preform and subsequently cooling the preform before the step of positioning the preform within the mold.
10. The method as set forth in claim 1 further including the step of forming a chamfer on an inward end of the preform to minimize the propagation of molten metal onto an inner surface of the preform.