Granted Patent B2

US 9,012,558 · App. 13/231,629 · Granted Apr 21, 2015

Abstract

Claims (58)

1. A one-part, moisture-curable, elastomeric, translucent coating composition comprising:

(a) a di-hydroxy-terminated dimethylpolysiloxane polymer having a viscosity of less than about 5,000 cps at 25 degrees Celsius;

(b) a reinforcing filler;

(c) an organic solvent;

(d) a polyalkoxysilane crosslinking agent;

(e) an organo-silane adhesion promoter; and,

(f) a titanium condensation cure catalyst,

wherein the composition is a one-part, moisture-curable, elastomeric, translucent coating composition.

2. The coating composition of claim 1 wherein the reinforcing filler (b) is fumed silica filler doubly treated with D4 and hexamethyldisilazane.

3. The coating composition of claim 1 wherein the organic solvent (c) is a linear aliphatic hydrocarbon.

4. The coating composition of claim 1 wherein the polyalkoxysilane crosslinking agent (d) is methyltrimethoxysilane.

5. The coating composition of claim 1 wherein the organo-silane adhesion promoter (e) is tris-trimethoxysilylpropylisocyanurate.

6. The coating composition of claim 1 wherein the titanium curing catalyst is di-isopropyl titanium bis-acetylacetonate.

7. The coating composition of claim 1 which has a stability of at least 1 month.

8. A process of forming a one-part, moisture-curable, elastomeric, translucent coating composition comprising:

combining the parts;

(a) a di-hydroxy-terminated dimethylpolysiloxane polymer having a viscosity of less than about 5,000 cps at 25 degrees Celsius;

(b) a reinforcing filler;

(c) an organic solvent;

(d) a polyalkoxysilane crosslinking agent;

(e) an organo-silane adhesion promoter; and,

(f) a titanium condensation cure catalyst

to provide a one-part moisture-curable, elastomeric, translucent coating composition.

9. The process of claim 8 further comprising:

applying the combined parts of the coating composition onto a substrate; and,

exposing the coating composition to sufficient moisture to provide for curing of the one-part, moisture-curable, elastomeric, translucent coating composition into a cured coating onto the substrate.

10. A substrate containing the cured coating made by the process of claim 9 .

11. The substrate of claim 10 wherein the coating has a modulus at 50% elongation per ASTM D-412 of from about 40 psi to about 150 psi.

12. The substrate of claim 10 wherein the coating has a Shore A durometer value per ASTM C-661 of from about 10 to about 40.

13. The substrate of claim 10 wherein the coating has a translucency which is greater than that of coating of an identical substrate coated with an identical coating composition.

14. The substrate of claim 10 wherein the coating has one or more of a durability or UV resistance which is greater than that of coating of an identical substrate coated with an identical coating composition.

15. The substrate of claim 10 wherein the coating provides water proofing protection for a longer period of time than that of coating of an identical substrate coated with an identical coating composition.

16. The substrate of claim 10 wherein the coating maintains the original appearance of the substrate more so than that of an identical substrate coated with an identical coating composition.

17. A method of treating a building façade comprising applying to an exterior portion of the building façade a one-part, moisture-curable, elastomeric, translucent coating composition comprising:

(a) a di-hydroxy-terminated dimethylpolysiloxane polymer;

(b) a reinforcing tiller;

(c) an organic solvent;

(d) a polyalkoxysilane crosslinking agent;

(e) an organo-silane adhesion promoter; and,

(f) a titanium condensation cure catalyst,

and curing the coating composition to provide a cured coating on the building facade.

18. A building facade containing the cured coating of claim 17 .

19. A one-part, moisture-curable, elastomeric, translucent coating composition comprising:

(a) a di-hydroxy-terminated dimethylpolysiloxane polymer;

(b) a reinforcing filler which is fumed silica filler doubly treated with D4 and hexamethyldisilazane;

(c) an organic solvent;

(d) a polyalkoxysilane crosslinking agent;

(e) an organo-silane adhesion promoter; and,

(f) a titanium condensation cure catalyst,

wherein the composition is a one-part, moisture-curable, elastomeric, translucent coating composition.

20. A one-part, moisture-curable, elastomeric, translucent coating composition comprising:

(a) a di-hydroxy-terminated dimethylpolysiloxane polymer;

(b) a reinforcing filler;

(c) an organic solvent;

(d) a polyalkoxysilane crosslinking agent;

(e) an organo-silane adhesion promoter; and,

(f) a titanium condensation cure catalyst which is di-isopropyl titanium bis-acetylacetonate,

wherein the composition is a one-part, moisture-curable, elastomeric, translucent coating composition.