Aqueous dispersion, its production method, and its use
View Patent ↗Aqueous dispersions including at least one thermoplastic resin; at least one dispersing agent; and water; wherein the dispersion has a pH of less than 12 are disclosed along with dispersions including at least one thermoplastic resin; at least one dispersing agent; and water wherein the dispersion has a volume average particle size of less than about 5 μm. Some dispersions include less than about 4 percent by weight of the dispersing agent based on the weight of the thermoplastic resin. Other dispersions include at least one propylene-rich alpha-olefin interpolymer; at least one dispersing agent; and water. Methods of making such dispersions are also described.
1. A coated substrate comprising:
a substrate; and
a coating composition associated with at least one surface of said substrate, wherein said coating composition comprises an aqueous dispersion compsrising the melt kneading of (A) at least one thermoplastic resin,wherein thermoplastic resin is (i) an interpolymer of ethylene with at least one comonomer selected from the group consisting of a C4-C20 linear, branched or cyclic diene, and a compound represented by the formula H2C═CHR wherein R is a C1-C20 linear, branched or cyclic alkyl group or a C6-C20 aryl group; or (ii) an interpolymer of propylene with at least one comonomer selected from the group consisting of ethylene, a C4-C20 linear, branched or cyclic diene, and a compound represented by the formula H2C═CHR wherein R is a C1-C20 linear, branched or cyclic alkyl group or a C6-C20 aryl group and (B) at least one dispersing agent; and (C) in the presence of water and optionally a basic substance in an extruder; wherein said aqueous dispersion has an average volume particle size diameter in the range of from 0.5 to 5 μm and a pH in the range of from 8 to 11.
2. The coated substrate of claim 1 , wherein said substrate is a film having a thickness in the range of from 1 to 30 μm.
3. The coated substrate of claim 1 , wherein the dispersing agent comprises at least one carboxylic acid, at least one salt of at least one carboxylic acid, at least one carboxylic acid ester, or at least one salt of at least one carboxylic acid ester.
4. The coated substrate of claim 1 , wherein the dispersing agent has fewer than 25 carbon atoms.
5. The coated substrate of claim 1 , wherein the dispersing agent is an ethylene carboxylic acid copolymer.
6. The coated substrate of claim 1 , wherein the dispersing agent is an ethylene acrylic acid copolymer or an ethylene methacrylic acid copolymer.