Vanadium-based frit materials, and/or methods of making the same
View Patent ↗Certain example embodiments relate to improved seals for glass articles. Certain example embodiments relate to a composition used for sealing an insulted glass unit. In certain example embodiments the composition includes vanadium oxide, barium oxide, zinc oxide, and at least one additional additive. For instance, another additive that is a different metal oxide or different metal chloride may be provided. In certain example embodiments, a vacuum insulated glass unit includes first and second glass substrates that are sealed together with a seal that includes the above-described composition.
1. A vacuum insulated glass (VIG) unit, comprising:
first and second substantially parallel, spaced apart glass substrates;
an edge seal provided around a periphery of the first and second substrates to form a hermetic seal therebetween and at least partially defining a gap between the first and second substrates,
wherein the gap is provided at a pressure less than atmospheric,
wherein the edge seal is formed from a frit material at least initially having a composition including:
(Ingredient)
(Normalized Mole %)
vanadium oxide
~45-50%,
barium oxide
~20-23%, and
zinc oxide
~19-21%; and
wherein the frit contains SnCl 2 in an amount no greater than 6%.
2. A vacuum insulated glass (VIG) window unit, comprising:
first and second substantially parallel, spaced apart thermally tempered glass substrates;
an edge seal provided around a periphery of the first and second thermally tempered glass substrates to form a hermetic seal therebetween and at least partially defining a gap between the first and second thermally tempered glass substrates,
wherein the gap of the vacuum insulated glass (VIG) window unit is provided at a pressure less than atmospheric,
wherein the edge seal is formed from a frit material at least initially having a composition consisting essentially of zinc oxide and:
(Ingredient)
(Normalized Mole %)
vanadium oxide
33-55%,
barium xoide
15-35%,
MoO 3
1-6%;
TeO 2
1-10%;
Ta 2 O 5
≧0.46%;
Nb 2 O 5
0.5-6%; and
wherein the materials with the three highest normalized mole % in the frit material are vanadium oxide, zinc oxide, and bariun oxide.
3. The VIG unit of claim 2 , wherein the frit material has a melting temperature less than or equal to about 400 degrees C.