Use of a shaped part made of a polyamide shaped component as an inliner for a conduit
View Patent ↗A pipe or hose composed of a polyamide moulding composition whose molecular weight has been increased by condensation, via addition of a compound having at least two carbonate units in a quantitative proportion of from 0.005 to 10% by weight, based on polyamide, where a) a starting polyamide moulding composition was provided, b) a mixture of the starting polyamide moulding composition and of the compound having at least two carbonate units was produced, c) the premix was, if desired, stored and/or transported, and d) the premix was then processed to give the moulding, this step being the first in which the increase of molecular weight by condensation occurred, the moulding being a pipe or hose whose external diameter is at least 25 mm is used as inliner for a pipeline.
1. A method for sealing a pipeline, comprising introducing inside of a pipe, an inner pipe having first and second open ends, said inner pipe comprising a polyamide moulding composition whose molecular weight has been increased by condensation, via the addition of a compound having at least two carbonate units in a quantitative proportion of from 0.005 to 10% by weight, based on polyamide prepared by a process comprising
a) mixing a starting polyamide moulding composition and said compound having at least two carbonate units forming a premix,
b) optionally, storing and/or transporting said premix, and
c) processing said premix to give a moulding, wherein an increase of molecular weight by condensation occurs for the first time,
said moulding being a pipe or hose whose external diameter is at least 25 mm.
2. The method according to claim 1 , wherein the external diameter of said moulding is at least 60 mm.
3. The method according to claim 1 , wherein the external diameter of said moulding is at least 110 mm.
4. The method according to claim 1 , wherein, said polyamide is prepared using a diamine or polyamine as a regulator.
5. The method according to claim 1 , wherein said compound having at least two carbonate units is used in the form of a masterbatch.
6. The method according to claim 1 , wherein said pipe transports at least one of district heating, fresh water, waste water, gas, oils, fuels, petrochemicals, brine, lyes, abrasive fluids and dusts.
7. The method according to claim 1 , wherein said inner pipe is hardened after introduction inside of said pipe.
8. The method according to claim 1 , wherein said inner pipe has an external diameter which is larger than an inner diameter of said pipe.
9. The method according to claim 1 , wherein said inner pipe is brought into contact with an inner wall of said pipe, after having been introduced inside of said pipe.
10. The method according to claim 1 , wherein said inner pipe is uniformly distributed over the inner periphery of said pipe.