Fluoropolymer composition
View Patent ↗A melt-mixed composition of non-melt flowable polytetrafluoroethylene (PTFE) and melt-fabricable perfluoropolymer is provided that exhibits thixotropy at increasing shear rate in the molten state and high elongation at break even at PTFE concentrations well above 4 wt %, based on the combined weight of the PTFE and the perfluoropolymer, e.g. at least 200% up to at least 30 wt % PTFE, the composition also exhibiting the structure of a dispersion of submicrometer-size particles of the PTFE in a continuous phase of the melt-fabricable perfluoropolymer.
1. A method for forming a melt-mixed composition, comprising melt mixing: (i) submicrometer-size particles comprising non-melt flowable polytetrafluoroethylene and particles comprising melt-fabricable perfluoropolymer, or (ii) submicrometer-size core/shell particles having a non-melt flowable polytetrafluoroethylene core and a melt-fabricable perfluoropolymer shell, at a shear rate of at least about 75 s −1 , wherein said melt-fabricable perfluoropolymer has a melt flow rate of from about 0.1 to 500 g/10 min as measured in accordance with Table 2 of ASTM D-1238-94a, wherein said non-melt flowable polytetrafluoroethylene has a melt creep viscosity of at least 1×10 6 Pa·s at 380° C. and constitutes at least about 4 wt % of the combined weight of said non-melt flowable polytetrafluoroethylene and said melt-fabricable perfluoropolymer, wherein said melt-mixed composition comprises a dispersion of said submicrometer-size particles comprising non-melt flowable polytetrafluoroethylene in a continuous phase comprising said melt-fabricable perfluoropolymer, and wherein said melt-mixed composition exhibits thixotropy when being subjected to increasing shear in the molten state.
2. The method of claim 1 , wherein said melt mixing comprises melt mixing fine powder formed by i) mixing aqueous dispersions of said non-melt flowable polytetrafluoroethylene and said melt-fabricable perfluoropolymer to form an aqueous dispersion mixture, ii) co-coagulating said aqueous dispersion mixture to form agglomerates comprising said non-melt flowable polytetrafluoroethylene and said melt-fabricable perfluoropolymer, and iii) drying said agglomerates to form said fine powder.
3. The method of claim 1 , wherein said non-melt flowable polytetrafluoroethylene is at least about 4 wt % to about 50 wt % of the combined weight of said non-melt flowable polytetrafluoroethylene and said melt-fabricable perfluoropolymer.