Polymer Composition and Method
Disclosed herein are compositions comprising a polymer and a carbamate. Also disclosed are methods of preparing these compositions, as well as methods of using these compositions to prepare additional polymer compositions. These compositions are useful as polymer compositions for molded articles or for preparing polymer compositions of molded articles.
1 . A composition comprising:
a) a polymer composition comprising a poly(arylene sulfide), a poly(arylene sulfone), a copolymer of a poly(arylene sulfide) and a poly(arylene sulfone), or any combination thereof; and
b) a carbamate having the formula R 4 (NHCO 2 R 3 ) y where y is 1, 2, or 3, R 3 is a C 1 to C 10 organic group, and R 4 is a C 1 to C 80 organic group.
2 . The composition of claim 1 , wherein R 3 is a C 1 to C 10 hydrocarbyl group or a C 1 to C 10 substituted hydrocarbyl group, and R 4 is a C 1 to C 30 hydrocarbon group or a C 1 to C 30 substituted hydrocarbon group.
3 . The composition of claim 1 , wherein R 3 is a C 1 to C 10 hydrocarbyl group, y is 2, and R 4 is a C 1 to C 30 hydrocarbylene group.
4 . The composition of claim 1 , wherein R 3 is a C 1 to C 10 hydrocarbyl group, y is 1, and R 4 is a C 1 to C 20 hydrocarbyl group.
5 . The composition of claim 1 , wherein R 3 is a C 1 to C 10 hydrocarbyl group, y is 1, and R 4 is a C 1 to C 20 hydrocarbylene group.
6 . The composition of claim 1 , wherein the polymer composition comprises polyphenylene sulfide, R 3 is a C 1 to C 10 hydrocarbyl group, y is 1, and R 4 is a C 1 to C 20 hydrocarbylene group.
7 . The composition of claim 1 , wherein y is 1 and R 4 is R x (R 1 O) 3-x SiR 2 —; and where x is 0, 1, 2, or 3; each R and R 1 independently is a C 1 to C 20 organic group; R 2 is a C 1 to C 20 organylene group; and R 3 is a C 1 to C 10 organic group.
8 . The composition of claim 7 , wherein x is 0, 1, or 2; each R and R 1 independently is a C 1 to C 10 hydrocarbyl group; R 2 is a C 1 to C 10 hydrocarbylene group; and R 3 is a C 1 to C 10 hydrocarbyl group.
9 . The composition of claim 7 , wherein x is 0; each R 1 is independently a methyl group or an ethyl group; R 2 is a methylene group, an ethylene group, or a propylene group; and R 3 is a methyl group or an ethyl group.
10 . The composition of claim 1 , wherein the carbamate comprises methyl-N-3-(trimethoxysilyl)-propylcarbamate, ethyl-N-3-(triethoxysilyl)propylcarbamate, methyl-N-3-(triethoxysilyl)propyl-carbamate, methyl-N-3-(methyldimethoxysilyl)propyl-carbamate, ethyl-N-3-(methyldiethoxysilyl)-propylcarbamate, or any combination thereof.
11 . The composition of claim 1 , wherein the polymer composition comprises poly(phenylene sulfide), and the carbamate is methyl-N-3-(trimethoxysilyl)propylcarbamate, ethyl-N-3-(triethoxysilyl)-propylcarbamate, methyl-N-3-(triethoxysilyl)propylcarbamate, methyl-N-3-(methyldimethoxysilyl)-propylcarbamate, ethyl-N-3-(methyldiethoxysilyl)propylcarbamate, or any combination thereof.
12 . The composition of claim 1 , wherein the composition further comprises a fire retardant, a stabilizer, an ultraviolet absorber, a lubricant, a pigment, a filler, or any combination thereof.
13 . A method of forming a composition comprising:
1) contacting
a) a polymer composition comprising a poly(arylene sulfide), a poly(arylene sulfone), a copolymer of a poly(arylene sulfide) and a poly(arylene sulfone), or any combination thereof; and
b) a carbamate having the formula R 4 (NHCO 2 R 3 ) y where y is 1, 2, or 3, R 3 is a C 1 to C 10 organic group, and R 4 is a C 1 to C 80 organic group;
to form a mixture and
2) melt processing the mixture.
14 . The method of claim 13 , wherein the polymer composition comprises poly(phenylene sulfide); the carbamate comprises methyl-N-3-(trimethoxysilyl)propylcarbamate, ethyl-N-3-(triethoxysilyl)-propylcarbamate, methyl-N-3-(triethoxysilyl)propylcarbamate, methyl-N-3-(methyldimethoxysilyl)-propyl-carbamate, ethyl-N-3-(methyldiethoxysilyl)propylcarbamate, or any combination thereof; and the poly(phenylene sulfide) and the carbamate are contacted at a poly(phenylene sulfide) to carbamate weight ratio from 1:1000 to 2:3
15 . The method of claim 13 , wherein the polymer composition comprises poly(phenylene sulfide); the carbamate comprises methyl-N-3-(trimethoxysilyl)propylcarbamate, ethyl-N-3-(triethoxysilyl)-propylcarbamate, methyl-N-3-(triethoxysilyl)propylcarbamate, methyl-N-3-(methyldimethoxysilyl)-propyl-carbamate, ethyl-N-3-(methyldiethoxysilyl)propylcarbamate, or any combination thereof; and the poly(phenylene sulfide) and the carbamate are contacted at a poly(phenylene sulfide) to carbamate weight ratio from 1:50 to 2:3.
16 . The method of claim 13 , wherein the polymer composition comprises poly(phenylene sulfide); the carbamate comprises methyl-N-3-(trimethoxysilyl)propylcarbamate, ethyl-N-3-(triethoxysilyl)-propylcarbamate, methyl-N-3-(triethoxysilyl)propylcarbamate, methyl-N-3-(methyldimethoxysilyl)-propyl-carbamate, ethyl-N-3-(methyldiethoxysilyl)propylcarbamate, or any combination thereof; and the poly(phenylene sulfide) and the carbamate are contacted at a poly(phenylene sulfide) to carbamate weight ratio from 1:1000 to 1:10.
17 . The method of claim 13 , wherein the mixture further comprise a fire retardant, a stabilizer, an ultraviolet absorber, a lubricant, a pigment, a filler, or any combination thereof.
18 . A method of forming a composition comprising:
1) contacting
a) a melt processed mixture formed from a first mixture comprising
i) a first polymer composition comprising a poly(arylene sulfide), a poly(arylene sulfone), a copolymer of a poly(arylene sulfide) and a poly(arylene sulfone), or any combination thereof, and
ii) a carbamate having the formula R 4 (NHCO 2 R 3 ) y where y is 1, 2, or 3, R 3 is a C 1 to C 10 organic group, and R 4 is a C 1 to C 80 organic group;
b) a second polymer composition comprising a poly(arylene sulfide), a poly(arylene sulfone), a copolymer of a poly(arylene sulfide) and a poly(arylene sulfone), or any combination thereof
to form a second mixture; and
2) melt processing the second mixture.
19 . The method of claim 18 , wherein weight ratio of the first polymer to the second polymer ranges from 1:1 to 1:50.
20 . The method of claim 18 , wherein one or more of the first mixture, the second mixture, the first polymer composition, or the second polymer composition further comprises one or more additives.
21 . The method of claim 18 , wherein the one or more of the first mixture, the second mixture, the first polymer composition, or the second polymer composition further comprises a fire retardant, a stabilizer, an ultraviolet absorber, a lubricant, a pigment, a filler, or any combination thereof.
22 . The method of claim 18 , wherein the one or more of the first mixture, the second mixture, the first polymer composition, or the second polymer composition further comprises a filler.
23 . The method of claim 18 , wherein the one or more of the first mixture, the second mixture, the first polymer composition, or the second polymer composition further comprises glass fibers, milled fibers, glass beads, asbestos, wollastonite, fiberglass, mica, talc, clay, calcium carbonate, magnesium hydroxide, silica, potassium titanate, fibers rockwool, aluminum flakes, zinc flakes, fibers of metals, carbon fibers, carbon black, or any combination thereof.
24 . The method of claim 18 , wherein the composition comprises from 2 to 60 weight percent filler.
25 . The method of claim 18 , wherein the composition has an improved flexural property or a tensile property.
26 . The method of claim 18 , wherein the first polymer composition, the second polymer composition, or the first polymer composition and the second polymer composition comprises poly(phenylene sulfide).
27 . A method of forming a composition comprising:
1) contacting
a) a first mixture comprising
i) a first polymer composition comprising a poly(arylene sulfide), a poly(arylene sulfone), a copolymer of a poly(arylene sulfide) and a poly(arylene sulfone), or any combination thereof, and
ii) a carbamate having the formula R 4 (NHCO 2 R 3 ) y where y is 1, 2, or 3, R 3 is a C 1 to C 10 organic group, and R 4 is a C 1 to C 80 organic group, and
b) a second polymer composition comprising a poly(arylene sulfide), a poly(arylene sulfone), a copolymer of a poly(arylene sulfide) and a poly(arylene sulfone), or any combination thereof,
to form a second mixture; and
2) melt processing the second mixture.
28 . The method of claim 27 , wherein one or more of the first mixture, the second mixture, the first polymer composition, or the second polymer composition further comprises one or more additives.
29 . The method of claim 27 , wherein the composition comprises from 2 to 60 weight percent filler.
30 . The method of claim 27 , wherein the composition has an improved flexural property or a tensile property.
31 . The method of claim 27 , wherein the first polymer composition, the second polymer composition, or the first polymer composition and the second polymer composition comprises poly(phenylene sulfide).