INSTALLATION OF LEAKAGE BARRIERS TO ENHANCE YIELD OF MINERAL DEPOSITS IN UNLINED SOLAR POND SYSTEMS
Slurry walls and methods of using those slurry walls to seal unlined solar ponds are provided. The slurry walls are formed from a mixture comprising clay and cement in water. A trench is keyed into the dike surrounding the solar pond, down to a geotechnically predetermined level. The slurry is deposited into the trench and allowed to harden, after which it is covered with a membrane or other covering. The inventive slurry walls reduce, and preferably prevent, leakage of water from the solar pond.
1 . A method of reducing or preventing leakage from a solar pond, the method comprising forming a slurry wall in a dike adjacent said solar pond, said slurry wall being formed from a mixture comprising clay, cement, and water.
2 . The method of claim 1 , wherein said mixture comprises from about 3% to about 25% by weight cement, based upon the total weight of the mixture taken as 100% by weight.
3 . The method of claim 1 , wherein said cement is selected from the group consisting of Types II-V Portland cements, blast furnace slag cement, and mixtures thereof.
4 . The method of claim 3 , wherein said cement is a Type II-V, sulfate-resistant Portland cement.
5 . The method of claim 1 , wherein said mixture comprises from about 1% to about 15% by weight clay, based upon the total weight of the mixture taken as 100% by weight.
6 . The method of claim 1 , wherein said clay is selected from the group consisting of bentonite clay, modified bentonite clay, sepiolite clay, attapulgite clay, and mixtures thereof.
7 . The method of claim 1 , wherein said water comprises the following properties:
a pH of from about 6.0 to about 9.5;
a hardness of less than about 400 ppm;
an alkalinity of less than about 400 ppm;
a total dissolved solids of less than about 4,000 ppm;
a density of from about 1.0 gm/cc to about 1.04 gm/cc; and
an apparent viscosity of from about 0.8 cP to about 2 cP.
8 . The method of claim 1 , wherein said water comprises the following properties:
a pH of from about 7.0 to about 9.0;
a hardness of less than about 600 ppm;
an alkalinity of less than about 400 ppm;
a total dissolved solids of less than about 200,000 ppm;
a density of from about 1.05 gm/cc to about 1.21 gm/cc; and
an apparent viscosity of from about 0.8 cP to about 2 cP.
9 . The method of claim 1 , wherein said forming comprises:
forming a trench in said dike;
placing said mixture in said trench; and
allowing said mixture to harden in said trench to form said slurry wall.
10 . The method of claim 9 , said slurry wall having a top portion and further comprising covering said top portion.
11 . The method of claim 1 , said solar pond having a perimeter, and said slurry wall being formed along said entire perimeter.
12 . The method of claim 1 , wherein said slurry wall has a permeability of less than about 1×10 −4 cm/sec.
13 . The method of claim 1 , wherein said slurry wall has an unconfined compressive strength of at least about 2.5 psig about 7 days after said slurry wall is formed.
14 . The method of claim 1 , wherein said slurry wall has a slake decay of less than about 25% by volume at about 30 days after said slurry wall is formed.
15 . The method of claim 1 , wherein said mixture is capable of hardening within about 7 days after said slurry wall is formed, as measured by a penetrometer.
16 . The method of claim 1 , wherein said mixture has a Marsh Funnel viscosity of from about 20 seconds to about 70 seconds.
17 . A modified solar pond comprising:
a solar pond having a dike adjacent thereto; and
a slurry wall in said dike, said slurry wall being formed from a mixture comprising clay, cement, and water.
18 . The pond of claim 17 , wherein said mixture comprises from about 3% to about 25% by weight cement, based upon the total weight of the mixture taken as 100% by weight.
19 . The pond of claim 17 , wherein said cement is selected from the group consisting of Types Portland cements, blast furnace slag cement, and mixtures thereof.
20 . The pond of claim 19 , wherein said cement is a Type II-V, sulfate-resistant Portland cement.
21 . The pond of claim 17 , wherein said mixture comprises from about 1% to about 15% by weight clay, based upon the total weight of the mixture taken as 100% by weight.
22 . The pond of claim 17 , wherein said clay is selected from the group consisting of bentonite clay, modified bentonite clay, sepiolite clay, attapulgite clay, and mixtures thereof.
23 . The pond of claim 17 , wherein said water comprises the following properties:
a pH of from about 6.0 to about 9.5;
a hardness of less than about 400 ppm;
an alkalinity of less than about 400 ppm;
a total dissolved solids of less than about 4,000 ppm;
a density of from about 1.0 gm/cc to about 1.04 gm/cc; and
an apparent viscosity of from about 0.8 cP to about 2 cP.
24 . The pond of claim 17 , wherein said water comprises the following properties:
a pH of from about 7.0 to about 9.0;
a hardness of less than about 600 ppm;
an alkalinity of less than about 400 ppm;
a total dissolved solids of less than about 200,000 ppm;
a density of from about 1.05 gm/cc to about 1.21 gm/cc; and
an apparent viscosity of from about 0.8 cP to about 2 cP.
25 . The pond of claim 17 , said slurry wall having a top portion that includes a covering thereon.
26 . The pond of claim 17 , said solar pond having a perimeter, and said slurry wall being along said entire perimeter.
27 . The pond of claim 17 , wherein said slurry wall has a permeability of less than about 1×10 −4 cm/sec.
28 . The pond of claim 17 , wherein said slurry wall has an unconfined compressive strength of at least about 2.5 psig about 7 days after said slurry wall is formed.
29 . The pond of claim 17 , wherein said slurry wall has a slake decay of less than about 20% by volume at about 30 days after said slurry wall is formed.
30 . The pond of claim 17 , wherein said mixture is capable of hardening within about 7 days after said slurry wall is formed, as measured by a penetrometer.
31 . The pond of claim 17 , wherein said mixture has a Marsh Funnel viscosity of from about 20 seconds to about 70 seconds.
32 . A slurry wall formed from a hardened mixture, the mixture before hardening comprising:
from about 3% to about 25% by weight cement, based upon the total weight of the mixture taken as 100% by weight;
from about 1% to about 15% by weight clay, based upon the total weight of the mixture taken as 100% by weight; and
water.
33 . The wall of claim 32 , wherein said cement is selected from the group consisting of Types II-V Portland cements, blast furnace slag cement, and mixtures thereof.
34 . The wall of claim 32 , wherein said clay is selected from the group consisting of bentonite clay, modified bentonite clay, sepiolite clay, attapulgite clay, and mixtures thereof.
35 . The wall of claim 32 , wherein said water comprises the following properties:
a pH of from about 6.0 to about 9.5;
a hardness of less than about 400 ppm;
an alkalinity of less than about 400 ppm;
a total dissolved solids of less than about 4,000 ppm;
a density of from about 1.0 gm/cc to about 1.04 gm/cc; and
an apparent viscosity of from about 0.8 cP to about 2 cP.
36 . The wall of claim 35 , wherein said mixture comprises Portland Cement and bentonite.
37 . The wall of claim 36 , wherein said mixture comprises about 17% by weight Portland Cement and about 6% by weight benonite, based upon the total weight of the mixture taken as 100% by weight.
38 . The wall of claim 32 , wherein said water comprises the following properties:
a pH of from about 7.0 to about 9.0;
a hardness of less than about 600 ppm;
an alkalinity of less than about 400 ppm;
a total dissolved solids of less than about 200,000 ppm;
a density of from about 1.05 gm/cc to about 1.21 gm/cc; and
an apparent viscosity of from about 0.8 cP to about 2 cP.
39 . The wall of claim 38 , wherein said mixture comprises Portland Cement, blast furnace slag cement, and sepiolite.
40 . The wall of claim 39 , wherein said mixture comprises about 1% by weight Portland Cement, about 12.5% by weight blast furnace slag cement, and about 5.5% by weight sepiolite, based upon the total weight of the mixture taken as 100% by weight.
41 . The wall of claim 32 , wherein said slurry wall has a permeability of less than about 1×10 −4 cm/sec.
42 . The wall of claim 32 , wherein said slurry wall has an unconfined compressive strength of at least about 2.5 psig about 7 days after said slurry wall is formed.
43 . The wall of claim 32 , wherein said slurry wall has a slake decay of less than about 20% by volume at about 30 days after said slurry wall is formed.
44 . The wall of claim 32 , wherein said mixture is capable of hardening within about 7 days after said slurry wall is formed, as measured by a penetrometer.
45 . The wall of claim 32 , wherein said mixture has a Marsh Funnel viscosity of from about 20 seconds to about 70 seconds.