Adhesive composition and optical member using the same

1. An adhesive composition, comprising:

a (meth)acrylate copolymer, an isocyanate crosslinking agent, and an imide-based crosslinking agent, the (meth)acrylate copolymer including:

a first (meth)acrylate resin of about 50 wt % to less than 100 wt % of the (meth)acrylate copolymer, the first (meth)acrylate resin having a glass transition temperature of about 200 K to about 250 K and a weight average molecular weight of about 800,000 to about 3,000,000 g/mol, and

a second (meth)acrylate resin of greater than 0 wt % to about 50 wt % of the (meth)acrylate copolymer, the second (meth)acrylate resin having a glass transition temperature of about 250 K to about 300 K and a weight average molecular weight of about 100,000 to about 800,000 g/mol, and

the adhesive composition providing an adhesive having a storage modulus of about 8×10 5 to about 1×10 8 dyne/cm 2 and a gel fraction of about 83% to about 95% as defined by Equation 1:

Gel fraction (%)=( A/B )×100,  [Equation 1]

in Equation 1, A is a mass of the adhesive measured after dissolving the adhesive at 23° C. for 48 hours in a solvent and then drying for 24 hours, and B is an initial mass of the adhesive formed from the adhesive composition.

2. The adhesive composition as claimed in claim 1 , wherein the second (meth)acrylate resin is copolymerized with a monomer having a glass transition temperature of about 253.15 K to about 423.15 K.

3. The adhesive composition as claimed in claim 2 , wherein the monomer having a glass transition temperature of about 253.15 K to about 423.15 K includes at least one of methylmethacrylate, methylacrylate, butylmethacrylate, and isobutylmethacrylate.

4. The adhesive composition as claimed in claim 1 , wherein:

the first (meth)acrylate resin is prepared by polymerization of a monomer mixture, the monomer mixture including a C 1-20 alkyl(meth)acrylate, a monomer having a hydroxyl group, and a monomer having a carboxyl group, and

the second (meth)acrylate resin is prepared by polymerization of another monomer mixture, the other monomer mixture including a C 1-20 alkyl(meth)acrylate, a monomer having a hydroxyl group, and a monomer having a carboxyl group.

5. The adhesive composition as claimed in claim 1 , wherein the adhesive composition includes 100 parts by weight of the (meth)acrylate copolymer; about 1 to about 10 parts by weight of the crosslinking agents; and about 0.01 to about 5 parts by weight of a silane coupling agent.

6. The adhesive composition as claimed in claim 1 , wherein a weight ratio of the isocyanate crosslinking agent to the imide-based crosslinking agent is from about 100:1 to about 350:1 in the cross-linking agent.

7. The adhesive composition as claimed in claim 1 , wherein the crosslinking agent includes about 3 to about 9 parts by weight of the isocyanate crosslinking agent and about 0.01 to about 1 parts by weight of the imide-based crosslinking agent, based on 100 parts by weight of the (meth)acrylate copolymer.

8. An optical member, comprising an adhesive layer on at least one side of an optical film, the adhesive layer being prepared from the adhesive composition as claimed in claim 1 .

9. The optical member as claimed in claim 8 , wherein the optical member has a brightness difference ΔL of less than about 1 between edge portions thereof and a center portion thereof, the brightness difference ΔL being defined by the following Equation 2:

Δ L =[( a+b+d+e )/4]− c,   [Equation 2]

in Equation 2, a, b, d, and e are each an average brightness of an area at an end of each respective side of the optical member, each area occupying 1/16 of a total area of the optical member, respectively, and c is an average brightness in an area occupying 1/32 of the total area at a center portion of the optical member.