Supported silver sulfide sorbent
View Patent ↗Synthesis of a support material impregnated with silver sulfide provides a sorbent composition. Generating the silver sulfide relies on reaction of sulfur dioxide and one of hydrogen gas and hydrogen sulfide in presence of the support material following silver loading of the support material. Contacting a fluid stream with the sorbent composition removes heavy metal from the fluid stream.
1. A method consisting essentially of:
forming from about 10.0 weight percent to about 20.0 weight percent silver oxide on a support;
converting the silver oxide to silver sulfide by reacting sulfur dioxide and one of hydrogen sulfide and hydrogen gas in presence of the support; and
contacting a mercury-containing fluid with the support that is impregnated with the silver sulfide for absorption of mercury from the fluid.
2. The method according to claim 1 , wherein all silver on the support is present as Ag 2 S monophase after the converting.
3. The method according to claim 1 , wherein silver content after the converting is about 15.0 weight percent of the support and is present only as Ag 2 S monophase.
4. The method according to claim 1 , wherein forming the silver oxide includes mixing the support with a solution containing silver from one of silver nitrate, silver halides and organo silver compounds.
5. The method according to claim 1 , wherein forming the silver oxide includes mixing the support with a solution formed by dissolution of a silver salt and then drying and calcining the support.
6. The method according to claim 1 , wherein forming the silver oxide includes mixing the support with a solution formed by dissolution of silver nitrate in water and then drying and calcining the support.
7. The method according to claim 1 , wherein the support is porous and includes one of zeolite, silica, alumina, activated carbon and clay.
8. The method according to claim 1 , wherein the converting the silver oxide to silver sulfide includes reacting the sulfur dioxide and the hydrogen sulfide in presence of the support.
9. The method according to claim 1 , wherein the converting the silver oxide to silver sulfide includes reacting the sulfur dioxide and the hydrogen gas in presence of the support.