Production method for sintered member
View Patent ↗A production method for a sintered member includes preparing a raw powder, compacting the raw powder into a green compact having pores at the surface thereof, and sintering the green compact into a sintered compact. The production method also includes sealing the pores exposed at the surface of the sintered compact by at least one of plastically deforming and melting the surface of the sintered compact. The production method further includes forging the sintered compact by using a lubricant after the sealing.
1. A production method for a sintered member, comprising:
preparing a raw powder;
compacting the raw powder into a green compact having pores at a surface thereof;
sintering the green compact into a sintered compact;
sealing the pores exposed at the surface of the sintered compact by performing shot peening to the surface of the sintered compact;
applying a lubricant to the sintered compact, the lubricant including at least two kinds of powders having different melting points, a first one of the powders having a lower melting point and a second one of the powders having a higher melting point;
heating the sintered compact such that the first one of the powders having the lower melting point is melted;
cooling the sintered compact such that the melted first one of the powders is solidified, thereby adhering the second one of the powders having the higher melting point to the sintered compact; and
cold forging the sintered compact after the cooling.
2. The production method for the sintered member according to claim 1 , wherein the shot peening is applied to at least a portion of the sintered compact, in which high strength is required as a product.
3. The production method for the sintered member according to claim 1 , wherein the shot peening is performed so as to seal the pores existing in an area of 25 to 150 μm in depth from the surface of the sintered member.
4. The production method for the sintered member according to claim 1 , wherein the shot peening is performed so as to seal the pores existing in an area of 50 to 150 μm in depth from the surface of the sintered member.
5. The production method for the sintered member according to claim 1 , wherein the first one of the powders having the lower melting point has a melting point of 60 to 140° C., and the second one of the powders having the higher melting point has a melting point of 200 to 250° C.
6. The production method for the sintered member according to claim 1 , wherein the second one of the powders having the higher melting point has an average particle size of 10 to 100 μm.
7. The production method for the sintered member according to claim 1 , wherein the second one of the powders having the higher melting point has an average particle size of 15 to 60 μm.
8. The production method for the sintered member according to claim 1 , wherein the shot peening is performed so that the sintered compact has a surface roughness Ra of 2 to 4 μm.
9. The production method for the sintered member according to claim 1 , wherein the cold forging is performed so that the sintered compact has a density ratio of not less than 97.8%.
10. The production method for the sintered member according to claim 1 , wherein the sintered compact is carburized and quenched and is then tempered after the cold forging.