Mixed carbon material including graphite powder cores and surface carbon material on a surface thereof and negative electrode for nonaqueous secondary battery
View Patent ↗The present invention provides a mixed carbon material which comprises carbon material A and carbon material B and which is a carbon material suitable for a negative electrode material which can provide a nonaqueous secondary battery having a low irreversible capacity and having a negative electrode with a high capacity and high charge acceptance. Carbon material A and carbon material B both have cores made of graphite powder and a surface carbon material in the form of at least one of amorphous carbon and turbostratic carbon adhered to or coated on at least a portion of the surface of the graphite powder. The compressed density is 1.80-1.90 g/cm 3 for carbon material A alone, 1.45-1.65 g/cm 3 for carbon material B alone, and 1.75-1.84 g/cm 3 for the mixed carbon material.
1. A mixed carbon material comprising carbon material A and carbon material B, wherein
carbon material A and carbon material B both have cores made of graphite powder and a surface carbon material adhered to and/or coated on at least a portion of the surface of the graphite powder,
the surface carbon material is at least one of amorphous carbon and turbostratic carbon,
the compressed density characteristic which is defined below is 1.80-1.90 g/cm 3 for carbon material A alone, 1.45-1.65 g/cm 3 for carbon material B alone, and 1.75-1.84 g/cm 3 for the mixed carbon material,
the average particle diameter of carbon material B is at most 14 μm and is smaller than the average particle diameter of carbon material A, and
the specific surface areas of carbon material A and carbon material B are at most 4 m 2 /g and at most 6 m 2 /g, respectively,
the compressed density characteristic being the density of a powder when 1.00 grams of the powder are packed into a cylindrical mold with a diameter of 15 mm, a pressing force of 8.7 kN is applied to the powder, and then the pressing force is reduced to 0.15 kN.
2. A mixed carbon material as set forth in claim 1 wherein the mixing ratio of carbon material A to carbon material B is from 90:10 to 60:40 as a mass ratio.
3. A negative electrode for a nonaqueous secondary battery having a negative electrode material including a mixed carbon material comprising carbon material A and carbon material B, wherein
carbon material A and carbon material B both have cores made of graphite powder and a surface carbon material adhered to and/or coated on at least a portion of the surface of the graphite powder,
the surface carbon material is at least one of amorphous carbon and turbostratic carbon,
the compressed density characteristic which is defined below is 1.80-1.90 g/cm 3 for carbon material A alone, 1.45-1.65 g/cm 3 for carbon material B alone, and 1.75-1.84 g/cm 3 for the mixed carbon material,
the average particle diameter of carbon material B is at most 14 μm and is smaller than the average particle diameter of carbon material A, and
the specific surface areas of carbon material A and carbon material B are at most 4 m 2 /g and at most 6 m 2 /g, respectively,
the compressed density characteristic being the density of a powder when 1.00 grams of the powder are packed into a cylindrical mold with a diameter of 15 mm, a pressing force of 8.7 kN is applied to the powder, and then the pressing force is reduced to 0.15 kN.
4. A negative electrode for a nonaqueous secondary battery as set forth in claim 3 wherein the mixing ratio of carbon material A to carbon material B is from 90:10 to 60:40 as a mass ratio.