A method for manufacturing a cutting tool includes the steps of providing a body of cermet or cemented carbide, having a cutting edge with an edge radius R e smaller than 40 μm, a flank a rake face, applying by PVD a single or a multilayer coating to at least a part of the surface of the body, comprising at least a part of the cutting edge and applying by PVD said single or multilayer coating, comprising PVD coating with at least one oxidic layer.
1. A method for manufacturing a cutting tool comprising the steps of
providing a body of cermet or cemented carbide, having a cutting edge with an edge radius R e smaller than 40 μm, a flank a rake face,
applying by PVD a single or a multilayer coating to at least a part of the surface of the body, comprising at least a part of the cutting edge, and
applying by PVD said single or multilayer coating, comprising PVD coating with at least one oxidic layer.
2. The method of claim 1 comprising applying by PVD said single or multilayer coating free of thermal cracks.
3. The method of claim 1 , wherein the oxidic layer comprises an electrically insulating oxide of at least one element selected from the group of transition metals of IV, V, VI group of the periodic system and Al, Si, Fe, Co, Ni, Y and La.
4. The method of claim 3 , said oxidic layer comprising a cubic structure.
5. The method of claim 3 , wherein said oxidic layer comprises a hexagonal crystal structure.
6. The method of claim 4 , wherein said oxidic layer comprises an (Al 1-x Cr x ) 2 O 3 compound.
7. The method of claim 5 , wherein said oxidic layer comprises an (Al 1-x Cr x ) 2 O 3 compound.
8. The method of claim 1 , wherein said oxidic layer comprises a corundum type structure.
9. The method of claim 8 , wherein said corundum type structure is corundum or is a multiple oxide having the following composition: (Me1 1-x Me2 x ) 2 O 3 , wherein 0.2≦x≦0.98 and Me1 and Me2 are different elements selected from the group consisting of Al, Cr, Fe, Li, Mg, Mn, Nb, Ti, Sb and V.
10. The method of claim 9 , wherein said corundum type structure is (AlCr) 2 O 3 or (AlV) 2 O 3 .
11. The method of claim 1 , wherein said oxidic layer comprises films of different oxides.
12. The method of claim 11 , further comprising PVD depositing an adhesion layer directly on said body and at least one hard wear protective layer between said adhesion layer and said oxidic layer, said adhesion layer and said hard wear protective layer comprising at least one element selected from the group of transition metals from group IV, V, VI of the periodic system of the elements and of Al, Si, Fe, Ni, Co, Y and La.
13. The method of claim 12 , wherein elements of said hard protective layer comprise compounds of N, C, O, B or a mixture thereof.
14. The method of claim 12 , wherein said at least one hard wear protective layer comprises at least one composition segregated film.
15. The method of claim 12 , wherein elements of said adhesion layer comprise compounds of N, C, O, or a mixture thereof.
16. The method of claim 12 , comprising depositing said adhesion layer with a thickness of between 0.1 μm and 1.5 μm.
17. The method of claim 12 , wherein said adhesion layer comprises a metallic layer directly on said surface of said body.
18. The method of claim 12 , further comprising depositing said hard wear protective layer between two consecutive oxidic layers.
19. The method of claim 1 , comprising PVD depositing said single or multilayer coating with a thickness of between 2 μm and 30 μm.
20. The method of claim 1 , further comprising providing said body of a material which is not binder enriched.
21. The method of claim 1 , further comprising providing said body of a material which is binder enriched.
22. The method of claim 1 , further comprising PVD coating said flank with said single or multilayer coating and with a first thickness and PVD coating said rake face with said single or multilayer coating with a second thickness, said first and second thicknesses being different.
23. The method of claim 22 , wherein said cutting tool is a milling tool having a quotient Q R/F =d Rake /d Flank <1, where d Rake is the overall coating thickness on the rake face and d Flank is the overall coating thickness on the flank.
24. The method of claim 22 , wherein the tool is a turning tool having a quotient Q R/F =d Rake /d Flank >1, where d Rake is the overall coating thickness on the rake face and d Flank is the overall coating thickness on the flank.
25. The method of claim 1 , wherein said cutting tool is an indexable insert.
26. The method of claim 12 , wherein the cutting tool is a gear cutting tool, a hob or shank type tool having said oxidic layer deposited as the outermost layer of said PVD coating.
27. The method of claim 26 , wherein said hard wear protective layer is deposited between said body and said oxidic layer and is of a material selected from the group consisting of TiN, TiC, TiCN, TiAlN, TiAlCN, AlCrN and AlCrCN.
28. The method of claim 1 , wherein said oxide layer is deposited by cathodic arc evaporation.
29. The method of claim 1 , wherein said single or multiple coating is deposited by cathodic arc evaporation.
30. The method of claim 29 , wherein said oxide layer is deposited in a pure oxygen atmosphere.