Method for manufacturing and handling elastomer thermoplastic gels
View Patent ↗Method of manufacturing granulates or continuous strips intended for feeding an extrusion machine, formed of a gel comprising at least, as majority elastomer, a styrene thermoplastic elastomer and more than 200 phr of an extender oil, each element of the granulate having a given surface area. The granulate element is sized so that the compactness, of a granulate element, is less than a value decreasing from 1500 m −1 to 375 m −1 and deposited on the surface of said granulates is an anti-tack agent having a value increasing from 2 cm 3 to 8 cm 3 per m 2 of granulate surface area, when the mean size of the particles of said anti-tack agent increases from a value of 1 μm to 100 μm.
1. A method of manufacturing granulates or pellets comprising forming granulates or pellets formed of an elastomer gel comprising a styrene thermoplastic elastomer and more than 200 per hundred of elastomer by weight of an extender oil, each granulate or pellet being dimensioned so that a compactness of each granulate or pellet is between 1500 m −1 and 375 m −1 , and, depositing on a surface of each of said granulates or pellets, are particles of an anti-tack agent having a volume between 2 cm 3 and 8 cm 3 per m 2 of surface area of each granulate or pellet, a mean size of the particles of said anti-tack agent being between 1 μm and 100 μm.
2. The manufacturing method according to claim 1 , wherein the mean size of the particles of said anti-tack agent is between 1 μm and 50 μm.
3. The manufacturing method according to claim 1 , wherein the styrene thermoplastic elastomer is selected from the group consisting of:
styrene/butadiene (SB),
styrene/isoprene (SI),
styrene/isobutylene (SIB),
styrene/ethylene/propylene (SEP),
styrene/ethylene/butylene (SEB),
styrene/butadiene/styrene (SBS),
styrene/isoprene/styrene (SIS),
styrene/butadiene/isoprene/styrene (SBIS),
styrene/isobutylene/styrene (SIBS),
styrene/ethylene/butylene/styrene (SEBS),
styrene/ethylene/propylene/styrene (SEPS),
styrene/ethylene/ethylene/propylene/styrene (SEEPS),
and blends of these copolymers.
4. The manufacturing method according to claim 1 , wherein the anti-tack agent contains greater than 80% of silica, mica, talc or zinc stearate.
5. The manufacturing method according to claim 1 , wherein each of the granulates or pellets has a substantially cylindrical shape.
6. The manufacturing method according to claim 5 , wherein each of the granulates or pellets is obtained by cutting sections of a continuous cylindrically-shaped strip.
7. A method of manufacturing a continuous strip comprising forming the continuous strip formed of an elastomer gel comprising a styrene thermoplastic elastomer and more than 200 per hundred of elastomer by weight of an extender oil, the continuous strip being dimensioned so that the continuous strip has a compactness of between 1500 m and 375 m, and, depositing on a surface of the strip, are particles of an anti-tack agent having a volume between 2 cm 3 and 8 cm 3 per m 2 of surface area of the continuous strip, a mean size of the particles of said anti-tack agent being between 1 μm and 100 μm.
8. The manufacturing method according to claim 7 , wherein the mean size of the particles of said anti-tack agent is between 1 μm and 50 μm.
9. The manufacturing method according to claim 7 , wherein the styrene thermoplastic elastomer is selected from the group consisting of:
styrene/butadiene (SB),
styrene/isoprene (SI),
styrene/isobutylene (SIB),
styrene/ethylene/propylene (SEP),
styrene/ethylene/butylene (SEB),
styrene/butadiene/styrene (SBS),
styrene/isoprene/styrene (SIS),
styrene/butadiene/isoprene/styrene (SBIS),
styrene/isobutylene/styrene (SIBS),
styrene/ethylene/butylene/styrene (SEBS),
styrene/ethylene/propylene/styrene (SEPS),
styrene/ethylene/ethylene/propylene/styrene (SEEPS),
and blends of these copolymers.
10. The manufacturing method according to claim 7 , wherein the anti-tack agent contains greater than 80% of silica, mica, talc or zinc stearate.