Powder coating composition comprising a polyester and a β-hydroxyalkylamide as crosslinker
View Patent ↗The invention relates to a thermosetting powder coating composition comprising a crosslinker and a polyester, wherein the polyester has functional groups which functional groups are capable of reacting with β-hydroxyalkylamide groups, wherein the polyester is prepared from at least the following monomers: neopentylglycol, a difunctional alcohol other than neopentylglycol; isophthalic acid, terephthalic acid, optionally adipic acid and a branching monomer chosen from the group of an at least trifunctional carboxylic acid, an at least trifunctional alcohol, an at least trifunctional hydroxy carboxylic acid and mixtures thereof, wherein the amount of difunctional alcohol other than neopentylglycol in the polyester ranges from 1 to 50% w/w based on the polyester, wherein the amount of isophthalic acid in the polyester ranges from 6 to 35% w/w based on the polyester, wherein the polyester has a functionality of at least 2.1, wherein the crosslinker is a compound having β-hydroxyalkylamide groups. This thermosetting powder coating composition has the ability to be cured at low temperature, while at the same time being able provide powder coatings having at least two of the following three properties: limited blooming to no blooming, an acceptable smoothness, sufficient impact resistance.
1. A thermosetting powder coating composition comprising a crosslinker and a polyester, wherein
the crosslinker is a compound having β-hydroxyalkylamide groups, and wherein
the polyester is a carboxylic acid functional polyester, and wherein
the polyester has functional groups capable of reacting with β-hydroxyalkylamide groups, and wherein
the polyester is prepared from at least the following monomers: neopentylglycol, a difunctional alcohol other than neopentyl glycol (DFA); isophthalic acid (IPA), terephthalic acid (TPA), optionally adipic acid, and a branching monomer selected from the group consisting of at least trifunctional carboxylic acid, an at least trifunctional alcohol, at least trifunctional hydroxy carboxylic acid, and mixtures thereof, and wherein
the DFA is present in the polyester from 1 to 50% w/w, and wherein
the IPA is present in the polyester from 6 to 30% w/w, and wherein
the molar ratio of TPA to IPA is at least 1.1, and wherein
the polyester has a functionality of at least 2.1 and at most 4.0, and wherein
the polyester has an acid value of at most 65 mg KOH/g, and wherein
the polyester has a hydroxyl value of at most 14 mg KOH/g, and wherein
the polyester has a glass transition temperature of at least 20° C. and of at most 120° C. measured via DSC at a heating rate of 5° C./min, and wherein
the polyester has a viscosity of at most 200 Pa·s measured at 160° C. using a cone and plate rheometer Brookfield CAP 2000+ Viscometer with spindle CAP-S-05 at 21 rpm and a shear rate 70 s-1 and wherein
% w/w is based on the polyester.
2. The thermosetting powder coating composition according to claim 1 , wherein the amount of IPA in the polyester ranges from 7 to 30% w/w.
3. The thermosetting powder coating composition according to claim 1 , wherein the amount of adipic acid in the polyester ranges from 1 to 10% w/w.
4. The thermosetting powder coating composition according to claim 1 , wherein IPA is present in the polyester in an amount of at most 40% mole based on the aromatic acid monomer.
5. The thermosetting powder coating composition according to claim 1 , wherein the polyester has a theoretical number average molecular weight ranging from 1000 to 10000 g/mol.
6. The thermosetting powder coating composition according to claim 1 , wherein the polyester has a functionality of at most 3.
7. The thermosetting powder coating composition according to claim 1 , wherein the polyester has an acid value of at least 15 mg KOH/g.
8. The thermosetting powder coating composition according to claim 1 , wherein the polyester has an acid value of at least 30 mg KOH/g.
9. The thermosetting powder coating composition according to claim 1 , wherein the polyester has an acid value of at most 60 mg KOH/g.
10. The thermosetting powder coating composition according to claim 1 , wherein the DFA is selected from the group consisting of ethylene glycol, neopentyl glycol-hydroxypivalic acid ester, 1,6-hexanediol and mixtures thereof.
11. The thermosetting powder coating composition according to claim 1 , wherein the DFA is 1,6-hexanediol.
12. The thermosetting powder coating composition according to claim 1 , wherein the thermosetting powder coating composition has a glass transition temperature of at least 20° C. and of at most 100° C.
13. The thermosetting powder coating composition according to claim 1 , wherein the ratio between the amount of the polyester and the amount of crosslinker is in the range of from 85:15 to 99:1.
14. The thermosetting powder coating composition according to claim 1 , wherein the polyester has a theoretical number average molecular weight ranging from 1000 to 10000 g/mol, and wherein the polyester has an acid value of at least 15 mg KOH/g, and wherein the thermosetting powder coating composition has a glass transition temperature of at least 20° C. and of at most 100° C., and wherein the ratio between the amount of the polyester and the amount of crosslinker is in the range of from 85:15 to 99:1.
15. The thermosetting powder coating composition according to claim 1 , wherein the polyester has a theoretical number average molecular weight ranging from 1000 to 10000 g/mol, and wherein the polyester has a functionality of at most 3, and wherein the polyester has an acid value of at least 15 mg KOH/g, and wherein the thermosetting powder coating composition has a glass transition temperature of at least 20° C. and of at most 100° C., and wherein the ratio between the amount of the polyester and the amount of crosslinker is in the range of from 85:15 to 99:1.
16. The thermosetting powder coating composition according to claim 1 , wherein the polyester has a theoretical number average molecular weight ranging from 1000 to 10000 g/mol, and wherein the polyester has an acid value of at least 30 mg KOH/g, and wherein the thermosetting powder coating composition has a glass transition temperature of at least 20° C. and of at most 100° C., and wherein the ratio between the amount of the polyester and the amount of crosslinker is in the range of from 85:15 to 99:1.
17. The thermosetting powder coating composition according to claim 1 , wherein the polyester has a theoretical number average molecular weight ranging from 1000 to 10000 g/mol, and wherein the polyester has a functionality of at most 3, and wherein the polyester has an acid value of at least 30 mg KOH/g, and wherein the thermosetting powder coating composition has a glass transition temperature of at least 20° C. and of at most 100° C., and wherein the ratio between the amount of the polyester and the amount of crosslinker is in the range of from 85:15 to 99:1.
18. The thermosetting powder coating composition according to claim 1 , wherein the amount of IPA in the polyester ranges from 7 to 30% w/w and the amount of adipic acid in the polyester ranges from 1 to 10% w/w.
19. The thermosetting powder coating composition according to claim 14 , wherein the amount of adipic acid in the polyester ranges from 1 to 10% w/w.
20. The thermosetting powder coating composition according to claim 15 , wherein the amount of adipic acid in the polyester ranges from 1 to 10% w/w.
21. The thermosetting powder coating composition according to claim 16 , wherein the amount of adipic acid in the polyester ranges from 1 to 10% w/w.
22. The thermosetting powder coating composition according to claim 17 , wherein the amount of adipic acid in the polyester ranges from 1 to 10% w/w.
23. The thermosetting powder coating composition according to claim 1 , wherein the DFA is 1,6-hexanediol.
24. The thermosetting powder coating composition according to claim 15 , wherein the DFA is 1,6-hexanediol.
25. The thermosetting powder coating composition according to claim 16 , wherein the DFA is 1,6-hexanediol.
26. The thermosetting powder coating composition according to claim 17 , wherein the DFA is 1,6-hexanediol.
27. The thermosetting powder coating composition according to claim 18 , wherein the DFA is 1,6-hexanediol.
28. The thermosetting powder coating composition according to claim 19 , wherein the DFA is 1,6-hexanediol.
29. The thermosetting powder coating composition according to claim 20 , wherein the DFA is 1,6-hexanediol.
30. The thermosetting powder coating composition according to claim 21 , wherein the DFA is 1,6-hexanediol.
31. The thermosetting powder coating composition according to claim 22 , wherein the DFA is 1,6-hexanediol.
32. The thermosetting powder coating composition according to claim 2 , wherein the amount of DFA in the polyester ranges from 1 to 11% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
33. The thermosetting powder coating composition according to claim 26 , wherein the amount of DFA in the polyester ranges from 1 to 11% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
34. The thermosetting powder coating composition according to claim 27 , wherein the amount of DFA in the polyester ranges from 1 to 11% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
35. The thermosetting powder coating composition according to claim 28 , wherein the amount of DFA in the polyester ranges from 1 to 11% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
36. The thermosetting powder coating composition according to claim 29 , wherein the amount of DFA in the polyester ranges from 1 to 11% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
37. The thermosetting powder coating composition according to claim 30 , wherein the amount of DFA in the polyester ranges from 1 to 11% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
38. The thermosetting powder coating composition according to claim 31 , wherein the amount of DFA in the polyester ranges from 1 to 11% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
39. The thermosetting powder coating composition according to claim 2 , wherein
the amount of adipic acid in the polyester ranges from 1 to 10% w/w, and wherein
the polyester has a viscosity of at most 56 Pa·s, and wherein either
i) The DFA is present in the polyester in an amount from 8 to 11% w/w, when the DFA is 2-methyl-1,3-propanediol; or
ii) the DFA is present in the polyester in an amount from 1 to 10% w/w, when the DFA is other than 2-methyl-1,3-propanediol.
40. The thermosetting powder coating composition according to claim 19 , wherein
the amount of adipic acid in the polyester ranges from 1 to 10% w/w, and
wherein
the polyester has a viscosity of at most 56 Pa·s,
and wherein either
i) the DFA is present in the polyester in an amount from 8 to 11% w/w, when the DFA is 2-methyl-1,3-propanediol; or
ii) the DFA is present in the polyester in an amount from 1 to 10% w/w, when DFA is other than 2-methyl-1,3-propanediol.
41. The thermosetting powder coating composition according to claim 20 , wherein
the amount of adipic acid in the polyester ranges from 1 to 10% w/w, and
wherein
the polyester has a viscosity of at most 56 Pa·s,
and wherein either
i) the DFA is present in the polyester in an amount from 8 to 11% w/w, when the DFA is 2-methyl-1,3-propanediol; or
ii) the DFA is present in the polyester in an amount from 1 to 10% w/w, when the DFA is other than 2-methyl-1,3-propanediol.
42. The thermosetting powder coating composition according to claim 21 , wherein
the amount of adipic acid in the polyester ranges from 1 to 10% w/w, and
wherein
the polyester has a viscosity of at most 56 Pa·s,
and wherein either
i) the DFA is present in the polyester in an amount from 8 to 11% w/w, when the DFA is 2-methyl-1,3-propanediol; or
ii) the DFA is present in the polyester in an amount from 1 to 10% w/w, when the DFA is other than 2-methyl-1,3-propanediol.
43. The thermosetting powder coating composition according to claim 22 , wherein
the amount of adipic acid in the polyester ranges from 1 to 10% w/w, and
wherein
the polyester has a viscosity of at most 56 Pa·s,
and wherein either
i) the DFA is present in the polyester in an amount from 8 to 11% w/w, when the DFA is 2-methyl-1,3-propanediol; or
ii) the DFA is present in the polyester in an amount from 1 to 10% w/w, when the DFA is other than 2-methyl-1,3-propanediol.
44. The thermosetting powder coating composition according to claim 1 , wherein the DFA is present in the polyester in an amount from 1 to 5% w/w when the DFA is other than 2-methyl-1,3-propanediol, and wherein the amount of IPA in the polyester ranges from 7 to 30% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
45. The thermosetting powder coating composition according to claim 1 , wherein the DFA is present in the polyester in an amount from 1 to 5% w/w when the DFA is other than 2-methyl-1,3-propanediol, and wherein the amount of IPA in the polyester ranges from 7 to 30% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
46. The thermosetting powder coating composition according to claim 19 , wherein the DFA is present in the polyester in an amount from 1 to 5% w/w when the DFA is other than 2-methyl-1,3-propanediol, and wherein the amount of IPA in the polyester ranges from 7 to 30% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
47. The thermosetting powder coating composition according to claim 20 , wherein the DFA is present in the polyester in an amount from 1 to 5% w/w when the DFA is other than 2-methyl-1,3-propanediol, and wherein the amount of IPA in the polyester ranges from 7 to 30% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
48. The thermosetting powder coating composition according to claim 21 , wherein the DFA is present in the polyester in an amount from 1 to 5% w/w when the DFA is other than 2-methyl-1,3-propanediol, and wherein the amount of IPA in the polyester ranges from 7 to 30% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
49. The thermosetting powder coating composition according to claim 22 , wherein the DFA is present in the polyester in an amount from 1 to 5% w/w when the DFA is other than 2-methyl-1,3-propanediol, and wherein the amount of IPA in the polyester ranges from 7 to 30% w/w, and wherein the polyester has a viscosity of at most 56 Pa·s.
50. The thermosetting powder coating composition according to claim 1 , wherein the amount of the polyester is at least 90% w/w based on total amount of resins present in the thermosetting powder coating composition.
51. The thermosetting powder coating composition according to claim 1 , wherein the thermosetting powder coating composition further comprises a processing additive of general formula X n -Y m , wherein n is an integer from 1 to 3 and m is an integer from 1 to 4, wherein the processing additive has a glass transition temperature ranging from 30 to 90° C., wherein Y is a polyester, polyacrylate or polyesterurethane, and wherein Y is connected via an ester bond to X, which is chosen from the group of phosphoric acid, phosphonic acid, sulphuric acid, sulphonic acid, sulfamine acid, boric acid, pyridine ethanol, 1,4,5,6,7,7-hexachlorobicyclo[2.2.1]-hept-5-ene-2,3-dicarboxylic acid (HET acid), maleic acid and combinations thereof, and wherein the processing additive is present in an amount of at least 0.5% w/w on the polyester.
52. The thermosetting powder coating composition according to claim 25 , wherein the thermosetting powder coating composition further comprises a processing additive of general formula X n -Y m , wherein n is an integer from 1 to 3 and m is an integer from 1 to 4, wherein the processing additive has a glass transition temperature ranging from 30 to 90° C., wherein Y is a polyester, polyacrylate or polyesterurethane, and wherein Y is connected via an ester bond to X, which is chosen from the group of phosphoric acid, phosphonic acid, sulphuric acid, sulphonic acid, sulfamine acid, boric acid, pyridine ethanol, 1,4,5,6,7,7-hexachlorobicyclo[2.2.1]-hept-5-ene-2,3-dicarboxylic acid (HET acid), maleic acid and combinations thereof, and wherein the processing additive is present in an amount of at least 0.5% w/w on the polyester.
53. A powder coating obtained by curing of a thermosetting powder coating composition according to claim 1 .
54. A powder coating obtained by curing of a thermosetting powder coating composition according to claim 52 .
55. A substrate fully or partially coated with a thermosetting powder coating composition according to claim 1 .
56. A substrate fully or partially coated with a thermosetting powder coating composition according to claim 52 .
57. A substrate fully or partially coated with a powder coating obtained by curing of a thermosetting powder coating composition according to claim 1 .
58. A substrate fully or partially coated with a powder coating obtained by curing of a thermosetting powder coating composition according to claim 52 .
59. A process for coating a substrate comprising the steps of:
i) applying the thermosetting powder coating composition according to claim 1 to a substrate such that the substrate is partially or fully coated with the thermosetting powder coating composition, and
ii) heating the obtained partially or fully coated substrate for a time from 1 minute to 60 minutes, and to a temperature from 140° C. to 225° C. to thereby obtain a coating that is at least partially cured.
60. A product comprising the partially or fully coated substrate according to claim 57 , wherein the product is a product for automotive applications, marine applications, aerospace applications, medical applications, defense applications, sports/recreational applications, architectural applications, bottling applications, household applications, or machinery applications.
61. A product comprising the partially or fully coated substrate according to claim 58 , wherein the product is a product for automotive applications, marine applications, aerospace applications, medical applications, defense applications, sports/recreational applications, architectural applications, bottling applications, household applications, or machinery applications.