Process for producing lithium composite metal oxide having layered structure
A method of producing a layered structure lithium mixed metal oxide, including a step of calcining a lithium mixed metal oxide raw material containing a transition metal element and a lithium element in a molar ratio of the lithium element to the transition metal element of 1 or more and 2 or less, in the presence of an inactive flux containing one or more compounds selected from the group consisting of a carbonate of M, a sulfate of M, a nitrate of M, a phosphate of M, a hydroxide of M, a molybdate of M, and a tungstate of M, wherein M represents one or more elements selected from the group consisting of Na, K, Rb, Cs, Ca, Mg, Sr and Ba.
1. A method of producing a layered structure lithium mixed metal oxide, comprising a step of calcining a lithium mixed metal oxide raw material comprising a transition metal element and a lithium element in a molar ratio of the lithium element to the transition metal element of 1 or more and 2 or less, in the presence of an inactive flux comprising Na 2 CO 3 or K 2 CO 3 or both, and a step of removing the inactive flux from the resultant after the calcination, by washing the resultant with distilled water.
2. The method according to claim 1 , wherein the lithium mixed metal oxide raw material is a mixture of a compound of lithium and a compound of the transition metal element.
3. The method according to claim 2 , wherein the compound of the transition metal element comprises Fe.
4. The method according to claim 3 , wherein the compound of the transition metal element further comprises one or more elements selected from the group consisting of Ni, Mn and Co.
5. The method according to claim 1 , wherein the inactive flux is present in an amount of 0.1 parts by weight or more and 100 parts by weight or less per 100 parts by weight of the lithium mixed metal oxide raw material at the commencement of calcination.
6. The method according to claim 1 , wherein a temperature of the calcination is in a range of from 200° C. to 1050° C.