Filled fluororesin sheet, process for producing the same, and gasket
Provided is a filled fluororesin sheet excellent in stress relaxation properties, in particular stress relaxation properties at a high temperature. The filled fluororesin sheet includes a fluororesin and an inorganic filler having a revised Mohs hardness of not less than 8, in a fluororesin:inorganic filler volume ratio of 30-55:70-45 (wherein the total of the two is 100).
1. A process for producing filled fluororesin sheets, comprising
a rolling step of rolling a sheet-forming resin composition which comprises a fluororesin, an inorganic filler having a revised Mohs hardness of not less than 8 that is selected from the group consisting of silicon carbide and α-alumina, and a processing aid and in which the volume ratio of the fluororesin and the inorganic filler (fluororesin:inorganic filler) is 30-55:70-45 (wherein the total of the two is 100),
a drying step in which the sheet that has been rolled in the rolling step is allowed to stand at ordinary temperature or is heated at a temperature not more than the melting point of the fluororesin, thereby removing the processing aid, and
a calcining step of heating the dried sheet at a temperature not less than the melting point of the fluororesin to sinter the sheet.
2. A filled fluororesin sheet produced by the process of claim 1 .
3. A gasket comprising the filled fluororesin sheet of claim 2 .