Removable adhesive label containing high tensile modulus polymeric film layer

1. A label, the label comprising:

(a) a film having a first surface and a second surface and comprising a first film layer; and

(b) a pressure sensitive adhesive layer having a first surface and a second surface and comprising an adhesive wherein the first surface of the adhesive layer is adhered to the second surface of the film;

wherein the first film layer comprises at least one thermoplastic polymer, wherein the first film layer has a tensile modulus (ASTM D882) in a machine direction or a transverse direction of at least 900 MPa after immersion in water at a temperature of about 80° C. for at least about 3 minutes, and the first film layer has an absolute areal dimensional change (ASTM D1204) of less than 5.0% after immersion in water at a temperature of about 80° C. for at least about 3 minutes,

wherein the thermoplastic polymer of the first film layer comprises a polymer selected from the group consisting of a (meth)acrylate polymer, a styrene polymer, a halogen-containing polymer, a polycarbonate, a polyacrylonitrile, an aromatic polyether, an aromatic polyimide, an aromatic polyamide-imide, and a mixture of two or more of any of the foregoing polymers,

wherein the pressure sensitive adhesive exhibits at least one of a decrease in adhesion strength at temperatures above a room or ambient temperature, a decrease in adhesion strength on contact with an aqueous caustic solution, and combinations thereof,

wherein the label has an opacity of 12% or less, and

wherein the first film layer is nonoriented.

2. The label of claim 1 wherein the thickness of the first film layer is greater than the thickness of the adhesive layer.

3. The label of claim 1 wherein the thickness of the first film layer is at least 5% greater than the thickness of the adhesive layer.

4. The label of claim 1 wherein the first film layer has a water absorption (ASTM 0570) of less than 2.1% by weight after immersion in water at a temperature of about 80° C. for at least about 2 hours.

5. The label of claim 1 wherein the first film layer is nonoriented.

6. The label of claim 1 wherein the film is amonolayered film.

7. The label of claim 1 wherein the film is a multilayered film.

8. The label of claim 1 wherein the first film layer comprises two or more layers.

9. The label of claim 1 wherein the film comprises a second film layer comprising at least one thermoplastic polymer wherein the second film layer has a property selected from

(i) a tensile modulus (ASTM D882) in a machine direction or a transverse direction of at least 900 MPa after immersion in water having a temperature of around 80° C. for a period of about 3 minutes; and

(ii) an absolute areal dimensional change (ASTM D1204) of less than about 5.0% after immersion in water having a temperature of around 80° C. for a period of about 3 minutes and a combination of the two foregoing properties.

10. The label of claim 9 wherein the second film layer comprises two or more layers wherein each of said two or more layers of the second film layer has a property selected from

(i) a tensile modulus (ASTM D882) in a machine direction or a transverse direction of at least 900 MPa after immersion in water having a temperature of around 80° C. for a period of about 3 minutes; and

(ii) an absolute areal dimensional change (ASTM D1204) of less than about 5.0% after immersion in water having a temperature of around 80° C. for a period of about 3 minutes;

and a combination of the two foregoing properties.

11. The label of claim 9 wherein the second film layer has a first surface and a second surface, the first film layer has a first surface and a second surface, the first surface of the first film layer underlies the second surface of the second film layer, and the first surface of the adhesive layer underlies the second surface of the first film layer.

12. The label of claim 9 wherein the first film layer has a first surface and a second surface, the second film layer has a first surface and a second surface, the first surface of the second film layer underlies the second surface of the first film layer, and the first surface of the adhesive layer underlies the second surface of the second film layer.

13. The label of claim 1 wherein the thermoplastic polymer of the first film layer is a polycarbonate.

14. A label, the label comprising:

(a) a film having a first surface and a second surface and comprising a first film layer, the first film layer comprising at least one thermoplastic polymer,

wherein the first film layer has a tensile modulus (ASTM D882) in a machine direction or a transverse direction of at least 900 MPa after immersion in water at a temperature of about 80° C. for at least about 3 minutes, and the first film layer has an absolute areal dimensional change (ASTM D1204) of less than 5.0% after immersion in water at a temperature of about 80° C. for at least about 3 minutes;

(b) a pressure sensitive adhesive layer having a first surface and a second surface, wherein the first surface of the adhesive layer is adhered to the second surface of the first film;

wherein the film comprises a second film layer comprising at least one thermoplastic polymer wherein the second film layer has a property selected from

(i) a tensile modulus (ASTM D882) in a machine direction or a transverse direction of at least 900 MPa after immersion in water having a temperature of around 80° C. for a period of about 3 minutes; and

(ii) an absolute areal dimensional change (ASTM D1204) of less than about 5.0% after immersion in water having a temperature of around 80° C. for a period of about 3 minutes and a combination of the two foregoing properties,

wherein the thermoplastic polymer of the first film layer comprises a polymer selected from the group consisting of a (meth)acrylate polymer, a styrene polymer, a halogen-containing polymer, a polycarbonate, a polyacrylonitrile, an aromatic polyether, an aromatic polyimide, an aromatic polyamide-imide, and a mixture of two or more of any of the foregoing polymers,

wherein the thermoplastic polymer of the second film layer comprises a polymer selected from the group consisting of a polyolefin, a (meth)acrylate polymer, a styrene polymer, a polyester, a halogen-containing polymer, a polycarbonate, a polyacrylonitrile, an aromatic polyether, an aromatic polyimide, an aromatic polyamide-imide, and a mixture of two or more of any of the foregoing polymers,

wherein the pressure sensitive adhesive exhibits at least one of a decrease in adhesion strength at temperatures above a room or ambient temperature, a decrease in adhesion strength on contact with an aqueous caustic solution, and combinations thereof,

wherein the label has an opacity of 12% or less, and

wherein the first film layer is nonoriented.

15. The label of claim 14 wherein the second film layer exhibits a water absorption of more than 1.6%.

16. The label of claim 14 wherein the second film layer exhibits a water absorption of less than 2.1%.

17. The label of claim 14 , wherein the first film layer exhibits a water absorption of less than 2.1%.

18. The label of claim 14 wherein the at least one layer has a linear shrinkage (ASTM D1204) at 100° C. in the machine direction and the transverse direction of less than 5%.

19. The label of claim 14 further comprising a print layer located between the layers of the film.

20. The label of claim 14 wherein the first film layer comprises two or more layers.

21. The label of claim 14 wherein the first surface of the first film layer underlies the second surface of the second film layer and wherein the tensile modulus of the first film layer is greater than or equal to the tensile modulus of the second film layer after immersion of the label in water having a temperature of around 80° C. for a period of about 3 minutes.

22. The label of claim 14 wherein the first and second film layers are nonoriented.

23. The label of claim 14 wherein the thermoplastic polymer of the first film layer is a polycarbonate.

24. The label of claim 14 wherein the thermoplastic polymer of the first film layer is a (meth)acrylate polymer.

25. The label of claim 1 or 14 wherein the label further comprises a release liner having a first surface and a second surface wherein the first surface of the release liner is releasably attached to the second surface of the adhesive layer.

26. A labeled container, comprising:

the label of claim 1 or 14 ; and

a container having a horizontal axis;

wherein the label is attached to the container wherein the second surface of the adhesive layer is adhesively joined to an outer surface of the container, and the machine direction or the transverse direction of the first film layer circumferentially follows the horizontal axis of the container.

27. The labeled container of claim 26 wherein the container is a cylindrically shaped container and the horizontal axis of the container is parallel to the circumference of the cylindrically shaped container.

28. A method of removing a label from a container, comprising:

(i) providing a labeled container of claim 26 ;

(ii) removing the label from the container by immersing the container with the attached label in a liquid wherein the temperature of the liquid is at least about 50° C. and the label detaches from the container.

29. The method of claim 28 wherein the liquid is water or a caustic aqueous solution.