Aerogel compositions and methods of making and using them
Compositions include an aerogel component and have low thermal conductivity. Methods for preparing slurries or composites include, for example combining the aerogel component with a surfactant, binder and other ingredients, such as, for instance, fibers. The compositions can be slurries that can be used in coating applications or self supporting rigid composites.
1. A composition comprising:
a) an aerogel component;
b) a surfactant;
c) a binder selected from the group consisting of cement, gypsum, lime, acrylate and any combination thereof; and
d) an ingredient selected from the group consisting of glass fibers, stone fibers, slag fibers, biosoluble ceramic fibers, and any combination thereof, wherein the composition has a thermal conductivity no greater than 50 mW/(m-k), measured according to ASTM C518.
2. The composition of claim 1 , wherein the fibers are present in the composition, when dried, in an amount within a range greater than 0% and less than 25% by weight of the composition.
3. The composition of claim 1 , wherein the fibers are present in the composition, when dried, in an amount of at least 25% by weight of the composition.
4. The composition of claim 1 , wherein (c) is either an inorganic binder or an inorganic binder-containing formulation, but not both.
5. The composition of claim 1 , wherein the composition is a dry mixture, a slurry or a composite.
6. The composition of claim 5 , wherein the slurry is pumpable, sprayable or paintable.
7. The composition of claim 5 , wherein the composition is a composite having a thermal conductivity that is no greater than about 35 MW/(m-K), measured according to ASTM C518.
8. The composition of claim 5 , wherein the composition is a composite having a thermal conductivity that is no greater than about 20 mW/(m-K), measured according to ASTM C518.
9. The composition of claim 5 , wherein the composite is a self-supporting rigid composite.
10. The composition of claim 5 , wherein the composite is a coating.
11. The composition of claim 1 , wherein the aerogel is a hydrophobic particulate silica aerogel.
12. The composition of claim 1 , wherein the binder-containing formulation is a grout formulation in accordance with European Standard EN 13888.
13. A self-supporting rigid composite comprising an aerogel component in particulate form, a binder selected from the group consisting of cement, gypsum, lime, acrylate and any combination thereof, and at least one other ingredient and having a thermal conductivity no greater than about 20 mW/(m-K), measured according to ASTM C518, wherein the at least one other ingredient includes fibers selected from the group consisting of glass fibers, stone fibers, slag fibers, biosoluble ceramic fibers, and any combination thereof.
14. The self-supporting rigid composite of claim 13 , wherein the self-supporting rigid composite includes a binder.
15. The self-supporting rigid composite of claim 14 , wherein the binder is selected from the group consisting of cement, gypsum, lime, acrylate and any combination thereof.
16. The self-supporting rigid composite of claim 15 , wherein the fibers are present in the composite in an amount within a range greater than 0% and less than 25% by weight of the composition.
17. The self-supporting rigid composite of claim 15 , wherein the fibers are present in the composite in an amount of at least 25% by weight of the composition.
18. The self-supporting rigid composite of claim 13 , wherein the composite has flame retarding properties.
19. The self-supporting rigid composite of claim 13 , wherein said composite has a compressive strength within the range of from about 0.05MPa to about 0.3MPa.
20. The self-supporting rigid composite of claim 13 , wherein said composite has a flexural strength of up to about 0.04MPa.
21. A composition comprising:
a) an aerogel component;
b) an acrylate in an amount of less than 11%;
c) a binder or a binder-containing formulation; and
d) at least one other ingredient comprising inorganic fibers, that are mineral wool fibers or a woven, non-woven or chopped form of continuously made glass or stone fiber, wherein the composition has a thermal conductivity no greater than 20 mW/(m-K), measured according to ASTM 0518.