Intumescent fireproofing systems and methods
Water-based intumescent fireproofing formulations are provided that exhibit excellent fireproofing properties while simultaneously significantly reducing and/or eliminating the potential for VOC release and exhibiting excellent hangability properties. The intumescent fireproofing formulation includes a coalescent that significantly reduces and/or eliminates the potential for VOC release and fiber constituents, e.g., fibers of greater than 0.2 mm in length. Exemplary coalescents have a boiling point of at least 180° C. and include bis(2-ethylhexanoate) triethyleneglycol and 2,2,4-trimethyl-1,3-pentanediolmono(2-methylproponate). Intumescent fireproofing formulations are also provided that include clay to further improve performance.
1. An intumescent fireproofing composition, comprising a formulation that includes:
a. a resin;
b. a coalescent; and
c. glass fibers of a predetermined size;
wherein the resin is a vinyl acetate copolymer;
wherein the coalescent exhibits a boiling point of greater than 240° C., the coalescent is effective to substantially reduce or eliminate the potential for volatile organic compound (VOC) release, and the coalescent is selected from a group consisting of 2,2,4-trimethyl-1,3-pentanediolmono(2-methylpropanoate) and bis(2-ethylhexanoate) triethylene glycol;
wherein the VOC is an organic compound exhibiting a boiling point greater than 250° C.;
wherein the predetermined size of the glass fibers is a length of between 0.2 mm and 3 mm; and
wherein the intumescent fireproofing composition delivers effective fireproofing and hangability performance, the hangability performance being defined by an absence of sliding or sagging of the intumescent fireproofing composition,
wherein sliding is a measure of movement of the intumescent fireproofing composition from an application position on a coated area to a position below the coated area due to gravity, and
wherein sagging is a measure of an increase in coating thickness from an applied thickness of the intumescent fireproofing composition to a final thickness defined by at least a two-fold increase in thickness from top to bottom of the coated area due to gravity.
2. The intumescent fireproofing composition according to claim 1 , wherein the formulation is water-based.
3. The intumescent fireproofing composition according to claim 1 , wherein the formulation further includes a defoamer and thickener.
4. The intumescent fireproofing composition according to claim 1 , wherein the formulation further includes at least one of titania, a polyphosphate, melamine and pentaerythritol.
5. The intumescent fireproofing composition according to claim 1 , wherein the glass fibers are included in the formulation at a level of between about 0.5% and 6% by weight.
6. The intumescent fireproofing composition according to claim 1 , wherein the predetermined size of the glass fibers is a length of between about 2 mm and 3 mm.
7. The intumescent fireproofing composition according to claim 1 , further comprising ceramic fibers selected from the group consisting of mineral wool, alumina, alumina-magnesia-silica, aluminosilicate, silica, zirconia and quartz fibers.
8. The intumescent fireproofing composition according to claim 1 , wherein the hangability performance is determined based on the intumescent fireproofing composition at the applied thickness of at least 0.25 mm.
9. The intumescent fireproofing composition according to claim 1 , wherein the formulation further comprises a constituent that is effective to decrease or eliminate potentially unpleasant odors.
10. The intumescent fireproofing composition according to claim 9 , wherein the constituent is selected from the group consisting of methyl salicylate, benzaldehyde, trans-cinnamonaldehyde and vanillin.
11. The intumescent fireproofing composition according to claim 1 , wherein the formulation further comprises clay.
12. The intumescent fireproofing composition according to claim 11 , wherein the clay is included in the formulation at a level of about one percent by weight.
13. A method for providing fireproofing protection to a substrate, comprising:
a. providing a fireproofing composition having a formulation that includes
(i) a resin; (ii) a coalescent; and (iii) glass fibers of a predetermined size;
b. applying the fireproofing composition to the substrate;
wherein the resin is a vinyl acetate copolymer;
wherein the coalescent exhibits a boiling point of greater than 240°C., the coalescent is effective to substantially reduce or eliminate the potential for volatile organic compound (VOC) release, and the coalescent is selected from a group consisting of 2,2,4-trimethyl-1,3-pentanediolmono(2-methylpropanoate) and bis(2-ethylhexanoate) triethylene glycol;
wherein the VOC is an organic compound exhibiting a boiling point greater than 250° C.;
wherein the predetermined size of the glass fibers is a length of between 0.2 mm and 3 mm; and
wherein the intumescent fireproofing composition delivers effective fireproofing and hangability performance when applied to the substrate, the hangability performance being defined by an absence of sliding or sagging of the intumescent fireproofing composition,
wherein sliding is a measure of movement of the intumescent fireproofing composition from an application position on a coated area to a position below the coated area due to gravity, and
wherein sagging is a measure of an increase in coating thickness from an applied thickness of the intumescent fireproofing composition to a final thickness defined by at least a two-fold increase in thickness from top to bottom of the coated area due to gravity.
14. The method according to claim 13 , wherein the formulation is water-based.
15. The method according to claim 13 , wherein the formulation further includes a defoamer and thickener.
16. The method according to claim 13 , wherein the formulation further includes at least one of titania, a polyphosphate, melamine and pentaerythritol.
17. The method according to claim 13 , wherein the glass fibers are included in the formulation at a level of between about 0.5% and 6% by weight.
18. The method according to claim 13 , wherein the predetermined size of the fibers is a length of between about 2 mm and 3 mm.
19. The method according to claim 13 , wherein the hangability performance is determined based on the intumescent fireproofing composition at an applied thickness of at least 0.25 mm.
20. The method according to claim 13 , wherein the formulation further comprises a constituent that is effective to decrease or eliminate potentially unpleasant odors.
21. The method according to claim 20 , wherein the constituent is selected from the group consisting of methyl salicylate, benzaldehyde, trans-cinnamonaldehyde and vanillin.
22. The method according to claim 13 , wherein the formulation further comprises clay.
23. The method according to claim 22 , wherein the clay is included in the formulation at a level of about one percent by weight.