Adhesive composition
An adhesive composition, an optical member, a surface protective film, and an adhesive sheet, the adhesive composition including 100 parts by weight of a (meth)acrylic copolymer having a weight average molecular weight of about 100,000 to about 2,000,000 g/mol; about 0.05 to about 5 parts by weight of a carbodiimide crosslinker, based on 100 parts by weight of the (meth)acrylic copolymer; and about 0.001 to about 5 parts by weight of an imidazole compound represented by Formula 1, based on 100 parts by weight of the (meth)acrylic copolymer: wherein, in Formula 1, R 1 , R 2 , and R 3 are each independently a hydrogen atom, a halogen atom, or a substituted or unsubstituted C1 to C10 straight or branched alkyl group.
1. An adhesive composition, comprising:
100 parts by weight of a (meth)acrylic copolymer having a weight average molecular weight of about 150,000 to about 950,000 g/mol;
about 0.05 to about 5 parts by weight of a carbodiimide crosslinker, based on 100 parts by weight of the (meth)acrylic copolymer; and
about 0.001 to about 5 parts by weight of an imidazole compound represented by Formula 1, based on 100 parts by weight of the (meth)acrylic copolymer:
wherein:
in Formula 1, R′, R 2 , and R 3 are each independently a hydrogen atom, a halogen atom, or a substituted or unsubstituted C1 to C10 straight or branched alkyl group,
the adhesive composition prepares an adhesive layer for a surface protective film, and
the adhesive layer has an adhesive strength of about 0.05 to about 0.3 N/25 mm according to JIS Z0237.
2. The adhesive composition as claimed in claim 1 , wherein the (meth)acrylic copolymer is prepared from a monomer mixture including:
about 0 to about 9 parts by weight of a carboxyl group containing monomer,
about 0 to about 9 parts by weight of a hydroxyl group containing (meth)acrylic monomer, and
about 82 to about 99.9 parts by weight of a (meth)acrylic acid ester monomer, a total amount of the carboxyl group containing monomer and the hydroxyl group containing (meth)acrylic monomer being greater than 0 parts by weight and a total amount of the carboxyl group containing monomer, the hydroxyl group containing (meth)acrylic monomer, and the (meth)acrylic acid ester monomer being 100 parts by weight.
3. An optical member comprising an adhesive layer prepared from an adhesive composition the adhesive composition including:
100 parts by weight of a (meth)acrylic copolymer having a weight average molecular weight of about 100,000 to about 2,000,000 g/mol;
about 0.05 to about 5 parts by weight of a carbodiimide crosslinker, based on 100 parts by weight of the (meth)acrylic copolymer; and
about 0.001 to about 5 parts by weight of an imidazole compound represented by Formula 1, based on 100 parts by weight of the (meth)acrylic copolymer:
wherein, in Formula 1, R 1 , R 2 , and R 3 are each independently a hydrogen atom, a halogen atom, or a substituted or unsubstituted C1 to C10 straight or branched alkyl group.
4. The optical member as claimed in claim 3 , wherein:
the (meth)acrylic copolymer has a weight average molecular weight of about 1,000,000 to about 1,800,000 g/mol, and
the adhesive layer has an adhesive strength of about 0.5 to about 9 N/25 mm according to JIS Z0237.
5. The optical member as claimed in claim 3 , wherein the adhesive layer has a gel fraction of about 50 to about 95% after forming the adhesive composition into an adhesive layer and leaving the adhesive layer at about 23° C. and about 50% RH for about 0.5 days.
6. An adhesive composition, comprising:
100 parts by weight of a (meth)acrylic copolymer having a weight average molecular weight of about 100,000 to about 2,000,000 g/mol;
about 0.05 to about 5 parts by weight of a carbodiimide crosslinker, based on 100 parts by weight of the (meth)acrylic copolymer; and
about 0.001 to about 5 parts by weight of an imidazole compound represented by Formula 1, based on 100 parts by weight of the (meth)acrylic copolymer:
wherein, in Formula 1, R′, R 2 , and R 3 are each independently a hydrogen atom, a halogen atom, or a substituted or unsubstituted C1 to C10 straight or branched alkyl group, and
wherein the (meth)acrylic copolymer is prepared from a monomer mixture including:
about 0 to about 9 parts by weight of a carboxyl group containing monomer,
greater than 0 to about 9 parts by weight of a hydroxyl group containing (meth)acrylic monomer, and
about 82 to about 99.9 parts by weight of a (meth)acrylic acid ester monomer, a total amount of the carboxyl group containing monomer, the hydroxyl group containing (meth)acrylic monomer, and the (meth)acrylic acid ester monomer being 100 parts by weight.
7. The adhesive composition as claimed in claim 6 , further comprising about 0.05 to about 5 parts by weight of an isocyanate crosslinker, based on 100 parts by weight of the (meth)acrylic copolymer.
8. The adhesive composition as claimed in claim 6 , further comprising a silane coupling agent.
9. A surface protective film comprising an adhesive layer prepared from the adhesive composition as claimed in claim 6 .
10. The surface protective film as claimed in claim 9 , wherein:
the (meth)acrylic copolymer has a weight average molecular weight of about 150,000 to about 950,000 g/mol, and
the adhesive layer has an adhesive strength of about 0.05 to about 0.3 N/25 mm according to JIS Z0237.
11. The surface protective film as claimed in claim 9 , wherein the adhesive layer has a gel fraction of about 70 to about 100% after forming the adhesive composition into an adhesive layer and leaving the adhesive layer at about 23° C. and about 50% RH for about 0.5 days.
12. An adhesive sheet comprising an adhesive layer prepared from the adhesive composition as claimed in claim 6 .
13. The adhesive sheet as claimed in claim 12 , wherein:
the (meth)acrylic copolymer has a weight average molecular weight of about 150,000 to about 950,000 g/mol, and
the adhesive layer has an adhesive strength of about 0.05 to about 20 N/25 mm according to JIS Z0237.
14. The adhesive sheet as claimed in claim 12 , wherein the adhesive layer has a gel fraction of about 70 to about 100% after forming the adhesive composition into an adhesive layer and leaving the adhesive layer at about 23° C. and about 50% RH for about 0.5 days.
15. The adhesive composition as claimed in claim 6 , wherein:
the (meth)acrylic copolymer has a weight average molecular weight of about 1,000,000 to about 1,800,000 g/mol,
the adhesive composition prepares an adhesive layer for an optical member, and
the adhesive layer has an adhesive strength of about 0.5 to about 9 N/25 mm according to JIS Z0237.
16. The adhesive composition as claimed in claim 15 , wherein the adhesive layer has a gel fraction of about 50 to about 95% after forming the adhesive composition into an adhesive layer and leaving the adhesive layer at about 23° C. and about 50% RH for about 0.5 days.
17. The adhesive composition as claimed in claim 6 , wherein:
the (meth)acrylic copolymer has a weight average molecular weight of about 150,000 to about 950,000 g/mol,
the adhesive composition prepares an adhesive layer for a surface protective film, and the adhesive layer has an adhesive strength of about 0.05 to about 0.3 N/25 mm according to JIS Z0237.
18. The adhesive composition as claimed in claim 17 , wherein the adhesive layer has a gel fraction of about 70 to about 100% after forming the adhesive composition into an adhesive layer and leaving the adhesive layer at about 23° C. and about 50% RH for about 0.5 days.
19. The adhesive composition as claimed in claim 6 , wherein:
the (meth)acrylic copolymer has a weight average molecular weight of about 150,000 to about 950,000 g/mol,
the adhesive composition prepares an adhesive layer for an adhesive sheet, and
the adhesive layer has an adhesive strength of about 0.05 to about 20 N/25 mm according to JIS Z0237.
20. The adhesive composition as claimed in claim 19 , wherein the adhesive layer has a gel fraction of about 70 to about 100% after forming the adhesive composition into an adhesive layer and leaving the adhesive layer at about 23° C. and about 50% RH for about 0.5 days.