View Patent ↗A roller bearing having two cooperating rolling parts of which one is of ceramic and the other of a steel. The steel part is of such structure and/or material and/or is so produced to cause residual compressive stresses to form beneath the contact surface of the steel part, at least in a load-free state, down to a depth.
1. A method of producing a steel rolling part of a roller bearing, the method comprising:
hardening the steel rolling part by a first hardening heat treating and tempering; and
subjecting the steel rolling part to a thermo-chemical heat treatment, following the tempering, by plasma nitriding an outer layer of the steel rolling part at a temperature of at least 400° C. so that compressive stresses in a martensitic microstructure of the steel rolling part of at least 300 MPa for a load-free outer layer of the steel rolling part from a surface to a depth of 40 μm from the surface are created and so that the outer layer has a hardness of at least 800 HVO.3 at a depth of about 0.2 mm from the surface,
wherein the tempering is performed at a temperature higher than the nitriding.
2. The method of claim 1 , wherein the first hardening heat treating includes austenitizing and quenching the steel rolling part.
3. The method of claim 2 , wherein the nitriding is performed in a temperature range of 400° C. to 600° C.