Adhesive composition
An adhesive composition, an optical member, a surface protective film, and an adhesive sheet, the adhesive composition including 100 parts by weight of a (meth)acrylic copolymer having a weight average molecular weight of about 100,000 to about 2,000,000 g/mol; about 0.01 to about 5 parts by weight of a peroxide crosslinking agent; and about 0.001 to about 5 parts by weight of a carbodiimide.
1. An adhesive composition, comprising:
100 parts by weight of a (meth)acrylic copolymer having a weight average molecular weight of about 100,000 to about 2,000,000 g/mol;
about 0.01 to about 5 parts by weight of a peroxide crosslinking agent; and
about 0.001 to about 5 parts by weight of a carbodiimide,
further comprising at least one of an isocyanate crosslinking agent and an imidazole compound, the imidazole compound being represented by Formula 1:
wherein, in Formula 1, R 1 , R 2 , and R 3 are each independently a hydrogen atom, a halogen atom, or a substituted or unsubstituted C 1 to C 10 straight or branched alkyl group, and wherein:
an adhesive layer formed from the adhesive composition has a gel fraction of at least about 50% under conditions of 23° C and 50% RH within a time period of about 12 hours or less after forming the adhesive composition into the adhesive layer.
2. The adhesive composition as claimed in claim 1 , wherein the (meth)acrylic copolymer is prepared from a monomer mixture including:
about 0 to about 9 parts by weight of a carboxyl group containing monomer,
about 0 to about 9 parts by weight of a hydroxyl group containing (meth)acrylic monomer, and
about 82 to about 99.9 parts by weight of a (meth)acrylic acid ester monomer, a total amount of the carboxyl group containing monomer and the hydroxyl group containing (meth)acrylic monomer being greater than 0 parts by weight and a total amount of the carboxyl group containing monomer, the hydroxyl group containing (meth)acrylic monomer, and the (meth)acrylic acid ester monomer being 100 parts by weight.
3. The adhesive composition as claimed in claim 1 , wherein the composition includes the isocyanate crosslinking agent, the isocyanate crosslinking agent being present in an amount of about 0.05 to about 5 parts by weight, based on 100 parts by weight of the (meth)acrylic copolymer.
4. The adhesive composition as claimed in claim 1 , wherein the composition includes the imidazole compound, the imidazole compound being present in an amount of about 0.05 to about 5 parts by weight, based on 100 parts by weight of the (meth)acrylic copolymer.
5. The adhesive composition as claimed in claim 1 , further comprising a silane coupling agent.
6. An optical member comprising an adhesive layer prepared from the adhesive composition as claimed in claim 1 .
7. The optical member as claimed in claim 6 , wherein:
the (meth)acrylic copolymer has a weight average molecular weight of about 1,000,000 to about 1,800,000 g/mol, and
the adhesive layer has an adhesive strength of about 0.5 to about 9 N/25 mm according to JIS Z0237.
8. The optical member as claimed in claim 6 , wherein the adhesive layer has a gel fraction of about 50 to about 95% under conditions of about 23° C and about 50%RH after forming the adhesive composition into the adhesive layer.
9. A surface protective film comprising an adhesive layer prepared from the adhesive composition as claimed in claim 1 .
10. The surface protective film as claimed in claim 9 , wherein:
the (meth)acrylic copolymer has a weight average molecular weight of about 150,000 to about 900,000 g/mol, and
the adhesive layer has an adhesive strength of about 0.05 to about 0.3 N/25mm according to JIS Z0237.
11. The surface protective film as claimed in claim 9 , wherein the adhesive layer has a gel fraction of about 70 to about 100% under conditions of about 23° C. and about 50% RH after forming the adhesive composition into the adhesive layer.
12. An adhesive sheet comprising an adhesive layer prepared from the adhesive composition as claimed in claim 1 .
13. The adhesive sheet as claimed in claim 12 , wherein:
the (meth)acrylic copolymer has a weight average molecular weight of about 150,000 to about 950,000 g/mol, and
the adhesive layer has an adhesive strength of about 0.05 to about 20 N/25 mm according to JIS Z0237.
14. The adhesive sheet as claimed in claim 12 , wherein the adhesive layer has a gel fraction of about 70 to about 100% under conditions of about 23° C. and about 50% RH after forming the adhesive composition into the adhesive layer.
15. The adhesive composition as claimed in claim 1 , wherein the adhesive layer has an adhesive strength of about 0.05 to about 0.3 N/25 mm according to JIS Z0237.
16. The adhesive composition as claimed in claim 1 , wherein the adhesive layer has an adhesive strength of about 0.5 to about 9 N/25 mm according to JIS Z0237.
17. The adhesive composition as claimed in claim 15 , wherein the gel fraction of the adhesive layer is about 70 to about 100% under conditions of 23° C. and 50% RH within the time period of about 12 hours or less after forming the adhesive composition into the adhesive layer.
18. The adhesive composition as claimed in claim 16 , wherein the gel fraction of the adhesive layer is about 50 to about 95% under conditions of 23° C. and 50% RH within the time period of about 12 hours or less after forming the adhesive composition into the adhesive layer.
19. An adhesive composition, comprising:
100 parts by weight of a (meth)acrylic copolymer having a weight average molecular weight of about 100,000 to about 2,000,000 g/mol;
about 0.01 to about 5 parts by weight of a peroxide crosslinking agent; and
about 0.001 to about 5 parts by weight of a carbodiimide,
further comprising at least one of about 0.05 to about 5 parts by weight of an isocyanate crosslinking agent and about 0.05 to about 5 parts by weight of an imidazole compound, the imidazole compound being represented by Formula 1:
wherein, in Formula 1, R 1 , R 2 , and R 3 are each independently a hydrogen atom, a halogen atom, or a substituted or unsubstituted C 1 to C 10 straight or branched alkyl group.