Making carbon articles from coated particles
View Patent ↗Methods and compositions relate to manufacturing a carbonaceous article from particles that have pitch coatings. Heating the particles that are formed into a shape of the article carbonizes the pitch coatings. The particles interconnect with one another due to being formed into the shape of the article and are fixed together where the pitch coatings along adjoined ones of the particles contact one another and are carbonized to create the article.
1. A method, comprising:
forming a shape of an article from particles separated from liquid of a suspension and provided by precipitation of pitch coatings onto solid cores dispersed in the suspension during the precipitation wherein lithium carbonate forms at least some of the solid cores; and
carbonizing the pitch coatings by heating the particles formed into the shape to above 400° C. such that the particles interconnected with one another due to being formed into the shape are fixed together where the pitch coatings along adjoined ones of the particles contact one another and are carbonized to create the article; and
further comprising removing the solid cores of the particles from the article to modify porosity of the article.
2. The method according to claim 1 , wherein the forming of the article relies on the pitch coatings to achieve interconnection of the particles without adding binder material to the particles.
3. The method according to claim 1 , wherein the forming the shape of the article includes pressing the particles together in a mold.
4. The method according to claim 1 , wherein carbon content of the pitch coatings prior to the carbonizing is at least 50%, by weight.
5. The method according to claim 1 , wherein the solid cores decompose during the carbonizing and at a temperature above a softening point of the pitch coatings.
6. The method according to claim 1 , further comprising dissolving with a solvent the solid cores of the particles from the article once the pitch coatings are carbonized.
7. The method according to claim 1 , further comprising controlling porosity of the article based at least in part on level of the pitch coatings on the solid cores.
8. The method according to claim 1 , wherein level of the pitch coatings on the solid cores is between 5 and 50 percent by weight of the particles.
9. The method according to claim 1 , wherein an average size of the particles is less than 1 millimeter.
10. The method according to claim 1 , wherein void space between the particles generated with the forming and prior to the carbonizing contributes to porosity of the article.
11. A method, comprising:
pressing a powder formed of particles having solid cores wherein lithium carbonate forms at least some of the solid cores that have a coating of pitch into a shape of an article with the particles interconnected from contact with one another under pressure; and
carbonizing the pitch by heating the powder pressed into the shape of the article to above 400° C. such that the pitch from adjoined ones of the particles is carbonized to provide the article with a cohesive network of carbonized material; and
further comprising removing the solid cores of the particles from the article to modify porosity of the article.
12. The method according to claim 11 , wherein the pressing leaves void space between the particles contributing to porosity of the article.
13. The method according to claim 11 , wherein the pressing is performed at a temperature above a softening point of the pitch so that voids among particles are filled with the pitch and the carbonizing converts the pitch to carbon providing the article with less than 10% porosity.
14. The method according to claim 11 , further comprising mixing the powder with a polymer solution to form a mixture that is then mechanically forced into the shape during the pressing, wherein the carbonizing of the pitch with the heating to above 400° C. also decomposes the polymer.