Filtration media for filtering particulate material from gas streams
View Patent ↗A composite fabric formed by depositing a web of nanofibers electroblown from a first polymer onto a first support web comprising fibers of larger average diameter than the nanofibers spun from a compatible material, in the absence of an adhesive between the webs, and solvent-bonding the webs together.
1. A process for forming a composite fabric, comprising electroblowing a web of polymeric nanofibers and a solvent therefor onto a moving support web comprising larger fibers spun from a material which is compatible with said nanofiber polymer, and applying a vacuum pressure between about 4 mm H 2 O and 170 mm H 2 O to the combined webs to solvent-bond the nanofiber web to the support web.
2. The process of claim 1 , wherein the applied vacuum pressure is between about 60 mm H 2 O and 170 mm H 2 O, to form a solvent-bonded nanofiber web/support web composite fabric.
3. The process of claim 1 , wherein the applied vacuum pressure is between about 4 mm H 2 O and 30 mm H 2 O, and further comprising depositing a second support web comprising larger fibers spun from a material which is compatible with said nanofiber polymer on said nanofiber web, to form a support web/nanofiber web/support web composite fabric, and passing said composite fabric through a consolidating nip, to solvent-bond the composite.
4. The process of claim 3 , further comprising drying the solvent-bonded composite fabric under vacuum to remove the solvent.