Copolymer blend compositions for use to increase paper filler content
View Patent ↗Methods for making a heterogeneous polymer blend comprising one or more anionic polymers, one or more cationic polymers, and one or more non-ionic polymers, which method comprises (a) adding to a non-neutral solution a first amount of polymerization initiator and one or more anionic or cationic monomers, wherein each monomer has the same charge; (b) a second amount of the polymerization initiator and one or more non-ionic monomers; (c) adding a third amount of the polymerization initiator and one or more ionic monomers that are oppositely charged from the monomers of (a); adding stepwise, a fourth amount of the polymerization initiator to react any residual monomer, and (e) neutralizing the resulting polymer blend. Also claimed are heterogeneous polymer blends containing polymers formed from one or more anionic, cationic, and non-ionic monomers, either polymerized in situ or separately and then combined.
1. A method of making a heterogeneous polymer blend, comprising:
a. adding to a non-neutral solution a first amount of a polymerization initiator and one or more anionic or cationic monomers, wherein each monomer has the same charge;
b. adding a second amount of the polymerization initiator and one or more non-ionic monomers to the solution;
c. adding a third amount of the polymerization initiator and one or more ionic monomers that are oppositely charged from the monomers of (a);
d. adding stepwise, a fourth amount of the polymerization initiator to react any residual monomer and resulting in the heterogeneous polymer blend; and
e. neutralizing, if necessary, the resulting heterogeneous polymer blend.
2. The method of claim 1 wherein
(a) the anionic monomer(s) are selected from the group consisting of: (1) acrylic acid, (2) methacrylic acid, (3) styrenesulfonic acid, (4) vinylsulfonic acid, (5) acrylamidomethylpropane sulfonic acid, and (6) mixtures thereof;
(b) the cationic monomer(s) are selected from the group consisting of: (1) diallyldimethylammonium chloride, (2) acryloylethyltrimethyl ammonium chloride, (3) methacryloylethyl trimethyl ammonium chloride, (4) acryloylethyltrimethylammonium sulfate, (5) methacryloylethyl trimethyl ammonium sulfate, (6) acrylamidopropyltrimethyl ammonium chloride, (7) methacrylamidopropyl trimethyl ammonium chloride, (8) non-quaternized forms of (2)-(7), (9) vinylformamide (subsequently hydrolyzed to vinylamine), and (10) mixtures thereof; and
(c) the nonionic monomer(s) are selected from the group consisting of: (1) acrylamide, (2) methacrylamide, (3) N-alkylacrylamide, (4) vinylformamide, and (5) mixtures thereof.
3. The method of claim 1 wherein the polymerization initiator is a water soluble azo initiator.
4. The method of claim 1 wherein the solution contains from about 10 mol % to about 30 mol % anionic monomer(s), from about 40 mol % to about 80 mol % non-ionic monomer(s), and from about 10 mol % to about 30 mol % cationic monomer(s).
5. The method of claim 2 wherein the anionic monomer comprises acrylic acid, wherein the cationic monomer comprises at least one of diallyldimethylammonium chloride or acrylamidopropyltrimethyl ammonium chloride and wherein the nonionic monomer of comprises acrylamide.
6. The method of claim 2 wherein the anionic monomer comprises styrenesulfonic acid or acrylamidomethylpropane sulfonic acid, wherein the cationic monomer comprises at least one of acryloylethyltrimethyl ammonium chloride or non-quaternized form of acryloylethyltrimethyl ammonium chloride, or vinylformamide (subsequently hydrolyzed to vinylamine), and wherein the nonionic monomer comprises vinylformamide.
7. A heterogeneous polymer blend, comprising:
a. one or more anionic polymers formed from at least one anionic monomer selected from the group consisting of: (1) acrylic acid, (2) methacrylic acid, (3) styrenesulfonic acid, (4) vinylsulfonic acid, (5) acrylamidomethylpropane sulfonic acid, and (6) mixtures thereof;
b. one or more cationic polymers formed from at least one cationic monomer selected from the group consisting of: (1) diallyldimethylammonium chloride , (2) acryloylethyltrimethyl ammonium chloride (3) methacryloylethyl trimethyl ammonium chloride, (4) acryloylethyltrimethylammonium sulfate (5) methacryloylethyl trimethyl ammonium sulfate, (6) acrylamidopropyltrimethyl ammonium chloride, (7) methacrylamidopropyl trimethyl ammonium chloride, (8) non-quaternized forms of (2)-(7), (9) vinylformamide (subsequently hydrolyzed to vinylamine), and (10) mixtures thereof;
c. one or more non-ionic polymers formed from at least one nonionic monomer selected from the group consisting of: (1) acrylamide, (2) methacrylamide, (3) N-alkylacrylamide, (4) vinylformamide, and (5) mixtures thereof, and
wherein the molar ratio of monomer used to make the homogeneous polymer blend is in the range of from about 10 to about 30 mol % anionic monomer, from about 40 to about 80 mol % nonionic monomer, and from about 10 to about 30 mol % cationic monomer.
8. The heterogeneous polymer blend of claim 7 , further comprising:
(d) one or more copolymers comprising at least one anionic monomer and at least one non-ionic monomer, and
(e) one or more copolymers comprising at least one cationic monomer and at least one non-ionic monomer.
9. The heterogeneous polymer blend of claim 8 , further comprising:
(f) one or more terpolymers comprising at least one anionic monomer, at least one cationic monomer, and at least one non-ionic monomer.
10. The heterogeneous polymer blend of claim 7 wherein the anionic monomer of a. comprises acrylic acid, wherein the cationic monomer of b. comprises at least one of diallyldimethylammonium chloride or acrylamidopropyltrimethyl ammonium chloride and wherein the nonionic monomer of c. comprises acrylamide.
11. The heterogeneous polymer blend of claim 7 wherein the anionic monomer of a. comprises styrenesulfonic acid or acrylamidomethylpropane sulfonic acid, wherein the cationic monomer of b. comprises at least one of acryloylethyltrimethyl ammonium chloride or non-quaternized form of acryloylethyltrimethyl ammonium chloride, or vinylformamide (subsequently hydrolyzed to vinylamine), and wherein the nonionic monomer of c. comprises vinylformamide.
12. A heterogeneous polymer blend, comprising:
a. one or more anionic polymers formed from at least one anionic monomer selected from the group consisting of: (1) acrylic acid, (2) methacrylic acid, (3) styrenesulfonic acid, (4) vinylsulfonic acid, (5) acrylamidomethylpropane sulfonic acid, and (6) mixtures thereof;
b. one or more cationic polymers formed from at least one cationic monomer selected from the group consisting of: (1) diallyldimethylammonium chloride , (2) acryloylethyltrimethyl ammonium chloride (3) methacryloylethyl trimethyl ammonium chloride, (4) acryloylethyltrimethylammonium sulfate (5) methacryloylethyl trimethyl ammonium sulfate, (6) acrylamidopropyltrimethyl ammonium chloride, (7) methacrylamidopropyl trimethyl ammonium chloride, (8) non-quaternized forms of (2)-(7), (9) vinylformamide (subsequently hydrolyzed to vinylamine), and (10) mixtures thereof;
c. one or more non-ionic polymers formed from at least one nonionic monomer selected from the group consisting of: (1) acrylamide, (2) methacrylamide, (3) N-alkylacrylarnide, (4) vinylformamide, and (5) mixtures thereof; wherein the active polymer concentration of the heterogeneous polymer blend is 10% or greater.
13. The heterogeneous polymer blend of claim 12 wherein the anionic monomer of a. comprises acrylic acid, wherein the cationic monomer of b. comprises at least one of diallyldimethylammonium chloride or acrylamidopropyltrimethyl ammonium chloride and wherein the nonionic monomer of c. comprises acrylamide.
14. The heterogeneous polymer blend of claim 12 wherein the anionic monomer of a. comprises styrenesulfonic acid or acrylamidomethylpropane sulfonic acid, wherein the cationic monomer of b. comprises at least one of acryloylethyltrimethyl ammonium chloride or non-quaternized form of acryloylethyltrimethyl ammonium chloride, or vinylformamide (subsequently hydrolyzed to vinylamine), and wherein the nonionic monomer of c. comprises vinylformamide.