Process for manufacturing agglomerated particles of tantalum, mixed tantalum powder and process for manufacturing same, tantalum pellet and process for manufacturing same, and capacitor
View Patent ↗A method for producing agglomerated tantalum particles, comprising: a step for grinding secondary tantalum particles, which are obtained by reducing a tantalum salt, and adding water thereto to give a water-containing mass; a step for drying said water-containing mass to give a dry mass; a step for sieving said dry mass to give spherical particles; and a step for heating said spherical particles. A mixed tantalum powder comprising a mixture of agglomerated tantalum particles (X) with agglomerated tantalum particles (Y), wherein said agglomerated tantalum particles (X) show a cumulative percentage of particles with particle size of 3 μm or less of 5 mass % or less after 25 W ultrasonic radiation for 10 min, while said agglomerated tantalum particles (Y) show a cumulative percentage of particles with particle size of 3 μm or less of 10 mass % or more after 25 W ultrasonic radiation for 10 min.
1. A process for manufacturing agglomerated particles of tantalum comprising the steps of: obtaining hydrated aggregates by pulverizing secondary particles of tantalum obtained by tantalum salt reduction with a pulverizer or granulator and adding water to said pulverizer or granulator before said pulverizing or during said pulverizing or both; obtaining dry aggregates by drying the hydrated aggregates; obtaining spheronized particles by passing the dry aggregates through one or more screens wherein said screens are vibrated; and heat treating the spheronized particles.
2. The process for manufacturing agglomerated particles of tantalum according to claim 1 , wherein secondary particles of tantalum obtained by a melt reduction of potassium fluorotantalate or secondary particles of tantalum obtained by a sodium reduction of tantalum chloride in the vapor phase are used as the secondary particles of tantalum.
3. The process for manufacturing agglomerated particles of tantalum according to claim 1 , wherein the powder that passes through said one or more screens is vibrated or rolled on a plate prior to said heat treating the spheronized particles.
4. The process for manufacturing agglomerated particles of tantalum according to claim 1 , which further includes subjecting the heat-treated spheronized particles to deoxidation treatment.
5. The process of claim 1 , wherein said one or more screens are vibrated in the vertical direction.
6. The process of claim 1 , wherein multiple screens are used.
7. The process of claim 1 , wherein said one or more screens are moved in the horizontal or vertical direction and are also moved in a circular manner.
8. The process of claim 1 , wherein the mode diameter of the spheronized particles is from 15 to 80 microns.
9. The method of claim 1 , wherein passage-assisting balls are present on the top of the one or more screens to increase vibration of the screens.
10. The process of claim 1 , wherein said pulverizing is achieved with said granulator equipped with at least one low-speed impeller and at least one high-speed impeller that rotates at a rotational speed that is at least 10 times higher than the rotational speed of said low-speed impeller.
11. The process of claim 1 , wherein said pulverizing is achieved with said granulator equipped with at least one low-speed impeller and at least one high-speed impeller that rotates at a rotational speed that is at least 30 times higher than the rotational speed of said low-speed impeller.
12. The process of claim 1 , wherein said pulverizing is achieved with said granulator equipped with at least one low-speed impeller and at least one high-speed impeller that rotates at a rotational speed that is at least 100 times higher than the rotational speed of said low-speed impeller.
13. The process of claim 1 , wherein said pulverizing is achieved with said granulator equipped with at least one low-speed impeller and at least one high-speed impeller that rotates at a rotational speed that is 30 to 1,000 times higher than the rotational speed of said low-speed impeller.