Methods for creating foam-like texture
Methods for creating a foam-like texture on an implantable material are provided. More particularly, methods for creating foam-like texture on implantable silicone materials are provided.
1. A method of making a textured breast implant, the method comprising:
applying a texturing material onto a mandrel having the shape of a breast implant;
placing a polyurethane foam sheet onto the texturing material;
causing integration between the texturing material and the polyurethane foam sheet by pressing the polyurethane foam sheet into the texturing material;
generating a composite of cured texturing material and polyurethane foam by curing the texturing material after the step of causing integration; and
after the step of generating the composite by curing, removing the polyurethane foam from the cured texturing material by application of a solvent of polyurethane to the composite, to thereby obtain a material having the shape of a breast implant and a surface texture characterized by interconnected pores.
2. The method of claim 1 , further comprising using clamps to stabilize the polyurethane foam sheet as it is placed onto and integrated with the texturing material.
3. The method of claim 1 , wherein the texturing material is a silicone material.
4. A method of producing a textured surface on an implantable breast prosthesis, the method comprising:
applying a base coat to a breast implant mandrel;
applying to the base coat, a texturing material comprising an uncured silicone dispersion;
placing a polyurethane foam sheet onto the texturing material;
applying pressure to integrate the polyurethane foam and the texturing material;
curing the texturing material with the polyurethane foam integrated thereto;
after the step of curing, removing the polyurethane foam from the cured texturing material by application of a solvent capable of dissolving polyurethane, to thereby obtain a material having the shape of a breast implant and a surface texture characterized by interconnected pores.
5. The method of claim 4 , wherein the thickness of the polyurethane foam sheet is between about 0.1 mm to about 250 mm and the thickness of the texturing material is between about 0.1 mm to about 50 mm.
6. The method of claim 1 wherein the solvent is hydrochloric acid.
7. The method of claim 1 wherein the solvent is hexane.
8. The method of claim 1 wherein the solvent is dimethyl sulfoxide (DMSO).
9. The method of claim 4 wherein the solvent is hydrochloric acid.
10. The method of claim 4 wherein the solvent is hexane.
11. The method of claim 4 wherein the solvent is dimethyl sulfoxide (DMSO).